Abstract:Hydroxyl-terminated polybutadiene (HTPB) is a flexible telechelic compound with a main chain containing a slightly cross-linked activated carbon-carbon double bond and a hydroxyl group at the end. Therefore, in this paper, HTPB was used as a terminal diol prepolymer, and sulfonate AAS and carboxylic acid DMPA were used as hydrophilic chain extenders to prepare low-temperature adaptive self-matting waterborne polyurethane (WPU). Due to the fact that the non-polar butene chain in the HTPB prepolymer cannot form a hydrogen bond with the urethane group, and the solubility parameter difference between the hard segment formed by the urethane group is large, the gap of T g between the soft and hard segments of the WPU increases by nearly 10 °C, with more obvious microphase separation. At the same time, by adjusting the HTPB content, WPU emulsions with different particle sizes can be obtained, thereby obtaining WPU emulsions with good extinction properties and mechanical properties. The results show that HTPB-based WPU with a certain degree of microphase separation and roughness obtained by introducing a large number of non-polar carbon chains has good extinction ability, and the 60° glossiness can be as low as 0.4 GU. Meanwhile, the introduction of HTPB can improve the mechanical properties and low temperature flexibility of WPU. The T g,s (the glass transition temperature of soft segment) of WPU modified by the HTPB block decreased by 5.82 °C, and the ΔT g increased by 21.04 °C, indicating that the degree of microphase separation increased. At -50 °C, the elongation at break and tensile strength of WPU modified by HTPB can still maintain 785.2% and 76.7 MPa, which are 1.82 times and 2.91 times those of WPU with only PTMG as soft segment, respectively. The self-matting WPU coating prepared in this paper can meet the requirements of severe cold weather and has potential application prospects in the field of finishing.

Influences of Soft/hard Chain Segment Ratio on Properties of Sulfonated Waterborne Polyurethane

Synthesis of High-Toughness Waterborne Polyurethane Utilizing Self-Emulsifying CO2-based Polyols

Effect of Water Content on the Aggregation and Adhesion Properties of Waterborne Polyurethane

Effect of Hydrophilic Chain-extending Agent on the Performance of High-solid Content Sulphonated Waterborne Polyurethane

Effects of aminopropyl-terminated polydimethylsiloxane on structure and properties of waterborne polyurethane-acrylate

Synthesis and Application of Hydroxyethyl Methacrylate Modified Waterborne Polyurethane

Influence of Siloxane Co-Segment Length and Content of Waterborne Polysiloxane-Urethane Copolymers on Their Water Resistance, Thermal Stability and Mechanical Properties

Studies on the influence of soft-segment structure on the properties of polyurethane adhesive

Synthesis and characterization of waterborne polyurethane emulsions based on poly(butylene itaconate) ester

Effects of Soft-Segments on the Structure and Properties of Polyurethane Emulsion

A novel strategy for preparation of solvent-free high-solid content water-based polyurethane

Preparation and Properties of High Solid Content and Low Viscosity Waterborne Polyurethane—Acrylate Emulsion with a Reactive Emulsifier

Preparation and characterization of high solid content cationic waterborne polyurethane with core‐shell structures

Preparation and properties of a novel waterborne fluorinated polyurethane–acrylate hybrid emulsion modified by long aliphatic chains

Synthesis and properties of waterborne polyurethane-based PTMG and PDMS as soft segment

Effects of Isosorbide on the Microphase Separation and Properties of Waterborne Polyurethane Coatings

A crosslinked waterborne poly(urethane‐urea) oligomer enables mechanically strong waterborne polyacrylate–poly(urethane‐urea) hybrid films with superior film‐forming ability

Preparation, Characterization, and Property Analysis of Environmentally Friendly Waterborne Polyurethane-Acrylate

Preparation and properties of waterborne siloxane-containing polyurethane for moisture permeable textile coating

Synthesis and characterization of hydroxyl-terminated polybutadiene modified low temperature adaptive self-matting waterborne polyurethane

Synthesis and Properties of Cationic Core-Shell Fluorinated Polyurethane Acrylate