Effect of Water Content on the Aggregation and Adhesion Properties of Waterborne Polyurethane

Zhen LUO,Can TAO,Xi-xi HAN,Jun-jie BAO,Qin CHENG,Yi-ping HUANG,Ge-wen XU

DOI: https://doi.org/10.3969/j.issn.1003-9015.2017.03.019

2017-01-01

Abstract:Waterborne polyurethane (WPUs) was prepared with poly (1,4-butanediol adipate)diol (PBA) as soft segments, and isophorone diisocyanate (IPDI), 2,2-dimethylol propionic acid (DMPA), diethylene glycol (DEG) and water as hard segments. Effects of water contents on WPUs performance were investigated. The structure and properties of WPUs were characterized by Fourier transform infrared spectroscopy (FT-IR), particle size analysis, gel permeation chromatography (GPC), differential scanning calorimetry (DSC), X-ray diffraction (XRD), thermal gravimetric analysis (TGA) and tensile tests. The results show that when water content increases, the intensity of hydrogen bonded N-H stretching vibration peaks increases and the crystallinity of WPUs decreases. Moreover, the average particle size and particle size distribution of emulsion increase, and the molecular weight and polydispersity of WPUs also increase. Meanwhile, the tensile strength, elongation at break and T-peel strength of the films increase first and then decrease. The results indicate that the tensile strength of the film reaches to a maximum value of 36.7 MPa and the maximum elongation at break is 1026.5% when the water content is 0.94%(wt). The T-peel strength of the waterborne polyurethane reaches to a maximum value of 1.9 N·cm-1 when the water content is 0.74%(wt).