Abstract:Polydimethylsiloxane (PDMS) is usually used to obtain favorable performances of waterborne polyurethane (WPU) such as higher hardness, exceptional thermal stability and lower interfacial tension. However, there is always a problem that waterborne polyurethane (WPU) often performs weak tensile strength, lower tenacity and brittle property at room temperature when polydimethylsiloxane (PDMS) is embedded into the backbone of polyurethane. The study aims to address the problem by constructing dual crosslinking structure, namely introducing trimethylolpropane as an intramolecular crosslinking agent into prepolymers and then adding waterborne polycarbodiimide (SK-400) as a post-crosslinking agent in order to further enlarge the degree of crosslinking and mainly make up for the shortcoming that mechanical property decreases when polydimethylsiloxane (PDMS) was inserted into molecule chains. Initially a novel inner-crosslinking prepolymer (SiWPU) comprising polydimethylsiloxane need to be synthesized successfully by inserting trimethylolpropane into prepolymers. Then the sample SiWPU-3 was picked out as a matrix resin and dropwise added polycarbodiimide (SK-400) as a post-crosslinking agent into the matrix resin (C–SiWPU). As pH was gradually lowering following the evaporation of triethylamine in the emulsion (C–SiWPU), carboxyl groups (COOH) in prepolymers started to react with SK-400 (NCN) to form twofold crosslinking structure. When 0%, 2%, 4%, 6%, and 8 wt% of waterborne polycarbodiimide (SK-400) was incorporated into the solution, the tensile strengths are 47.8 MPa, 57.7 MPa, 65 MPa, 57.6 MPa and 54.5 MPa and the elongation at break 732%, 756%, 798%, 707% and 700%. The crosslinking density of SiWPU-3 without the addition of waterborne polycarbodiimide (SK-400) is 3.86 × 10−3 mol/cm3. As 6 wt% of waterborne polycarbodiimide (SK-400) was added into the emulsion of SiWPU-3, the crosslinking density of C–SiWPU-6 (6 wt% SK-400) is 6.19 × 10−3 mol/cm3. The films show excellent extensibility and exceptional tenacity. Hence, the emulsion is able to be applied in leather industry.

Synthesis of High-Toughness Waterborne Polyurethane Utilizing Self-Emulsifying CO2-based Polyols

Synthesis of CO2-Derived, Siloxane-Functionalized Poly(ether Carbonate)s and Waterborne Polyurethanes

Synthesis and Characterization of Eugenol‐based Silicone Modified Waterborne Polyurethane with Excellent Properties

Synthesis and Application of Hydroxyethyl Methacrylate Modified Waterborne Polyurethane

Synthesis and modification of waterborne polyurethane derived from hybrid CO2-based polyols

Effect of Water Content on the Aggregation and Adhesion Properties of Waterborne Polyurethane

Synthesis and characterization of waterborne polyurethane emulsions based on poly(butylene itaconate) ester

A crosslinked waterborne poly(urethane‐urea) oligomer enables mechanically strong waterborne polyacrylate–poly(urethane‐urea) hybrid films with superior film‐forming ability

Synthesis and properties of waterborne polyurethane-based PTMG and PDMS as soft segment

Pickering emulsion approach: A novel strategy to fabricate waterborne polyurethane with enhanced abradability and water-resistance comparable to that of solvent-based coating

Synthesis and characterization of hydroxyl-terminated polybutadiene modified low temperature adaptive self-matting waterborne polyurethane

A novel method for the synthesis of solvent‐free and high‐solid‐content waterborne polyurethanes by introducing a small amount of polyethylene glycol

A novel strategy for preparation of solvent-free high-solid content water-based polyurethane

The tough, fluorescent and adhesive elastomer in aqueous dispersion: The contribution of aromatic amide-urea segments

Effects of aminopropyl-terminated polydimethylsiloxane on structure and properties of waterborne polyurethane-acrylate

Synthesis of waterborne polyurethane by inserting polydimethylsiloxane and constructing dual crosslinking for obtaining the superior performance of waterborne coatings

A bio-based waterborne polyurethane with high toughness, superior wear resistance, and water resistance enabled by sorbitol monooleate

Preparation and Properties of High Solid Content and Low Viscosity Waterborne Polyurethane—Acrylate Emulsion with a Reactive Emulsifier

Improving water resistance of waterborne polyurethane coating with high transparency and good mechanical properties

Enhanced mechanical strength and water resistance in waterborne polyurethanes through hydroxyl-functionalized MQ silicone resin modification

Preparation, Characterization, and Property Analysis of Environmentally Friendly Waterborne Polyurethane-Acrylate