Abstract:Polydimethylsiloxane (PDMS) is usually used to obtain favorable performances of waterborne polyurethane (WPU) such as higher hardness, exceptional thermal stability and lower interfacial tension. However, there is always a problem that waterborne polyurethane (WPU) often performs weak tensile strength, lower tenacity and brittle property at room temperature when polydimethylsiloxane (PDMS) is embedded into the backbone of polyurethane. The study aims to address the problem by constructing dual crosslinking structure, namely introducing trimethylolpropane as an intramolecular crosslinking agent into prepolymers and then adding waterborne polycarbodiimide (SK-400) as a post-crosslinking agent in order to further enlarge the degree of crosslinking and mainly make up for the shortcoming that mechanical property decreases when polydimethylsiloxane (PDMS) was inserted into molecule chains. Initially a novel inner-crosslinking prepolymer (SiWPU) comprising polydimethylsiloxane need to be synthesized successfully by inserting trimethylolpropane into prepolymers. Then the sample SiWPU-3 was picked out as a matrix resin and dropwise added polycarbodiimide (SK-400) as a post-crosslinking agent into the matrix resin (C–SiWPU). As pH was gradually lowering following the evaporation of triethylamine in the emulsion (C–SiWPU), carboxyl groups (COOH) in prepolymers started to react with SK-400 (NCN) to form twofold crosslinking structure. When 0%, 2%, 4%, 6%, and 8 wt% of waterborne polycarbodiimide (SK-400) was incorporated into the solution, the tensile strengths are 47.8 MPa, 57.7 MPa, 65 MPa, 57.6 MPa and 54.5 MPa and the elongation at break 732%, 756%, 798%, 707% and 700%. The crosslinking density of SiWPU-3 without the addition of waterborne polycarbodiimide (SK-400) is 3.86 × 10−3 mol/cm3. As 6 wt% of waterborne polycarbodiimide (SK-400) was added into the emulsion of SiWPU-3, the crosslinking density of C–SiWPU-6 (6 wt% SK-400) is 6.19 × 10−3 mol/cm3. The films show excellent extensibility and exceptional tenacity. Hence, the emulsion is able to be applied in leather industry.

Synthesis and modification of waterborne polyurethane derived from hybrid CO2-based polyols

Synthesis of CO2-Derived, Siloxane-Functionalized Poly(ether Carbonate)s and Waterborne Polyurethanes

Synthesis of High-Toughness Waterborne Polyurethane Utilizing Self-Emulsifying CO2-based Polyols

Synthesis and Characterization of Eugenol‐based Silicone Modified Waterborne Polyurethane with Excellent Properties

Polyhydroxyurethanes (PHUs) Derived from Diphenolic Acid and Carbon Dioxide and Their Application in Solvent- and Water-Borne PHU Coatings

Synthesis and Application of Hydroxyethyl Methacrylate Modified Waterborne Polyurethane

Preparation and properties study of waterborne polyurethane synthesized by mixing polyester diols and isocyanates

Synthesis of novel propylene carbonate diol(PCD)and application in CO2-based polyols waterborne polyurethane

Synthesis of poly (propylene carbonate) diol-based waterborne polyurethane modified by epoxy resin with anticorrosion properties

Improving water resistance of waterborne polyurethane coating with high transparency and good mechanical properties

Enhanced mechanical strength and water resistance in waterborne polyurethanes through hydroxyl-functionalized MQ silicone resin modification

Terpene derivative-containing silicone two-component waterborne polyurethane for coatings

Synthesis and properties of castor oil–based cationic waterborne polyurethane modified by epoxy resin

Synthesis and characterization of waterborne polyurethane emulsions based on poly(butylene itaconate) ester

Synthesis and properties of waterborne polyurethane-based PTMG and PDMS as soft segment

Synthesis and properties of CO2 copolymer-based waterborne polyurethane with high solid content

Synthesis and properties of polyurethane modified with an aminoethylaminopropyl-substituted polydimethylsiloxane. II. Waterborne polyurethanes

Synthesis of waterborne polyurethane by inserting polydimethylsiloxane and constructing dual crosslinking for obtaining the superior performance of waterborne coatings

A novel method for the synthesis of solvent‐free and high‐solid‐content waterborne polyurethanes by introducing a small amount of polyethylene glycol

Preparation and characterization of cationic waterborne polyurethanes containing a star-branched polydimethylsiloxane

Effects of aminopropyl-terminated polydimethylsiloxane on structure and properties of waterborne polyurethane-acrylate