Synthesis and properties of CO2 copolymer-based waterborne polyurethane with high solid content

Wenqi Xian,Jie Yuan,Zhengbin Xie,Wei Ou,Xiaoxuan Liu,Baohua Liu

DOI: https://doi.org/10.1007/s10965-021-02616-9

IF: 3.061

2021-06-16

Journal of Polymer Research

Abstract:A series of CO₂ copolymer-based waterborne polyurethanes with high solid content were successfully prepared by using CO₂ copolymer diol, isophorone diisocyanate, and dimethylol propionic acid as the donors of hydrophilic groups. In order to obtain of the emulsion with high solid content and good physical property, the synthesis conditions of CO₂ copolymer-based waterborne polyurethane were studied. The influence of dimethylol propionic acid content and synthesis process on the physical property of the emulsion was also investigated. Results show that CO₂ copolymer-based waterborne polyurethane with high solid content can be synthesized by chain expansion at relatively low temperature. The waterborne polyurethane emulsion particle size distribution was wide. As the content of hydrophilic groups in prepolymer increased, the viscosity and water absorption increased obviously, this is difficult to synthesize waterborne polyurethane with high solid content and low water absorption. Thermal gravimetric analysis shows that the higher the chain extending temperature of CO₂ copolymer-based waterborne polyurethane, the higher the thermal decomposition temperature. When the CO₂ molar content of CO₂ copolymer diol is about 30%, the CO₂ copolymer-based waterborne polyurethane has high strength and better water resistance.

polymer science