Abstract:Using hydroxypropyl terminated polydimethylsiloxane ( HP. PDMS ), isophorone diisocyanate and 2,2-bis( hydroxymethyl ) butyric acid as starting materials, silicone-polyurethane copolymer ( Si-PU ) latexes with particle diameter of about 50 nm were prepared via step-by-step feeding process followed by phase inversion technique in the absence of surfactant. Influences of the HP-PDMS content on the phase structure and the properties of the Si-PU latex films were investigated, and the difference between Si-PU and polyether polyurethane ( E-PU ) was emphasized. It was found that the content of PDMS in Si-PU could reach up to 65 wt%. Results of DSC analysis showed that, in comparison with the E-PU latex film, the Si-PU latex films exhibited well phase separation. Strong hydrogen bonding in Si-PU hard segments was confirmed by FTIR, which promoted the micro. phase separation in the latex films. On the contrary, strong hydrogen bonding existed in between the soft and hard segments in E-PU, which led to phase mixing and prevented the formation of phase separation structure. The Si-PU latex films were characterized by AFM tapping mode and the formation of sea. island phase separation was observed, and this kind of phase separation structure in the Si-PU latex films was rarely reported in the literature, in which the amorphous PDMS. enriched domains constituted the dispersed phases. With the increase in HP. PDMS content, the degree of phase separation in the Si-PU latex films increased as well, which led to the decrease of elastic modulus from 400.0 MPa to 32.2 MPa with an increase in elongation at break and in the flexibility. The initial decomposition temperature of the Si-PU latex films was at about 244 degrees C, which was 18 degrees C lower than that of the E-PU latex film due to the low degree of hydrogen bonding between the soft and the hard segments, whereas the thermal stability of Si-PU at high temperature zone was much better than E-PU. Compare to the E-PU latex film, a low water adsorption rate under 11% and a high contact angle above 94 degrees indicated excellent water resistance of the Si-PU latex films.

Influence of Siloxane Co-Segment Length and Content of Waterborne Polysiloxane-Urethane Copolymers on Their Water Resistance, Thermal Stability and Mechanical Properties

Synthesis of CO2-Derived, Siloxane-Functionalized Poly(ether Carbonate)s and Waterborne Polyurethanes

Synthesis of High-Toughness Waterborne Polyurethane Utilizing Self-Emulsifying CO2-based Polyols

Synthesis and Characterization of Eugenol‐based Silicone Modified Waterborne Polyurethane with Excellent Properties

Sturcture and Properties of New Aqueous Dispersion Polysiloxane-Polyuretane Copolymers

Synthesis and properties of waterborne polyurethane-based PTMG and PDMS as soft segment

Preparation and properties of waterborne siloxane-containing polyurethane for moisture permeable textile coating

Preparation and Properties of Waterborne Polysiloxaneurethane/Clay Nanocomposite

Synthesis of waterborne polyurethane by inserting polydimethylsiloxane and constructing dual crosslinking for obtaining the superior performance of waterborne coatings

Synthesis of Waterborne Polyurethane Modified by Nano-SiO2 Silicone and Properties of the WPU Coated RDX

Alkoxysilane Functionalized Polyurethane/Polysiloxane Copolymers: Synthesis and the Effect of End-Capping Agent

Synthesis and Properties of Triethoxysilane-Terminated Anionic Polyurethane and Its Waterborne Dispersions

Synthesis and Characterization of PDMS Modified UV-curable Waterborne Polyurethane Dispersions for Soft Tact Layers

Investigation on the Preparation of Silicone-polyurethane Latex, Phase Structure and Property of the Latex Films

The synthesis and properties of siloxane-urethane copolymers aqueous nanodispersion using hydroxyalkyl and hydrohxypolyester terminated polydimethylsiloxane

Moisture-cured Polyurethane/polysiloxane Copolymers: Effects of the Structure of Polyester Diol and NCO/OH Ratio

The Synthesis and Properties of Moisture-curing Polyurethane/Polysiloxane Copolymers

Effects of aminopropyl-terminated polydimethylsiloxane on structure and properties of waterborne polyurethane-acrylate

Terpene derivative-containing silicone two-component waterborne polyurethane for coatings

Preparation and characterization of cationic waterborne polyurethanes containing a star-branched polydimethylsiloxane

Synthesis And Surface Property Of Siloxane-Modified Aqueous Polyurethane