Preparation and Properties of Waterborne Polysiloxaneurethane/Clay Nanocomposite

高传花,倪加旎,郑强,陈世龙,林薇薇,屠军刚

DOI: https://doi.org/10.3969/j.issn.1009-4369.2010.01.004

2010-01-01

Abstract:A novel nanocomposite aqueous dispersion composed of waterborne polysiloxane-urethane/montmorillonite(WPSUR/MMT) was synthesized by self-made amino-terminated polydimethylsiloxane(NS) as chain extender.Wide angle X-ray diffraction(WXRD) and transmission electron microscopy(TEM) showed that MMT's ordered structure was destroyed after its intercalation with polyether,and random strips were scattered in WPSUR.Therefore,stripped type WPSUR/MMT nanocomposites were obtained.The experimental results showed that with the increase of the amount of MMT,the particle size of aqueous dispersion increased,apparent viscosity increased.With the same amount of MMT,the particle size of aqueous dispersion with NS as chain extender is lager than that with micromolecule as chain extender,its apparent viscosity is high.The introduction of MMT significantly improved the mechanical properties of WPSUR/MMT film.When the mass fraction of MMT was 1 %,the tensile strength and elongation at break of WPSUR/MMT film increased 22.8% and 9.6% compared to blank WPSUR,reinforcing and toughening the WPSUR.Both NS and MMT improved the heat resistance of WPSUR film when NS was used as chain extender.The weight loss peak temperature in the second phase of WPSUR/MMT(3%) film increased by 20℃.