Abstract:Two kinds of adsorbates—L-ascorbic acid and NaOH were used separately to investigate the effects of adsorbate distribution between ethanol bulk phase and the phase of water-rich layer adsorbed by the surface of SiO2 particles on the preparation of silver nanoparticles on SiO2 particles. When the adsorbate L-ascorbic acid was used, L-ascorbic distributes mainly in the ethanol bulk phase and thus the Ag particle generating reaction will take place in the ethanol bulk phase with the generated Ag particle size of about 18 nm. When the adsorbate NaOH was used, NaOH distributes mainly in the phase of water-rich layer adsorbed on the surface of SiO2 particles and thus the Ag particles generate in the water-rich adsorption layer with particle size of only about 5.4 nm. Since the NaOH concentration effects its distribution between the two phases of ethanol bulk phase and water-rich adsorption layer, the further experiments with changing NaOH concentration in the reaction system from 0.0170 to 0.404 g·L-1 were conducted. Results show that when concentration of NaOH in the system was increased from 0.0170 to 0.135 g·L-1, the NaOH concentration in the water-rich adsorption layer increases with the increase of NaOH concentration in the system gradually, which causes the generation of Ag grains gradually centralizes in the adsorption layer with the grain size decreases from 8 nm to 5 nm, and the Ag particles generated cover the SiO2 more uniformly. When NaOH concentration in the system was increased from 0.135 to 0.404 g·L-1, the amount of NaOH in the system is over the maximum NaOH capacity that can be contained in the water-rich adsorption layer and thus the NaOH concentration in ethanol bulk phase will increase to the limit, above which, the Ag generating reaction rate in it will accelerate more quickly than that in the water-rich adsorption layer, which causes the main generation zone of silver nanoparticles moves from water-rich adsorption layer to ethanol bulk phase gradually, and at the same time, the generated Ag grain size will increase from 5 nm to 12 nm.

Effects of Diethanolamine on the Evolution of Silver/titanium Dioxide Sol–gel Process

Effect of Interphase Distribution of Reactants in Binary Liquids on Preparation of Silver Nanoparticles on Silica Particles

Controllable Synthesis of SiO2 Nanoparticles: Effects of Ammonia and Tetraethyl Orthosilicate Concentration

Effect of Incorporation of Silver on the Electrical Properties of Sol-Gel-Derived Titania Film

Effects of Heat-Treatment Temperature on Preparation of the Sol-Gel-Derived Ag/TiO2 Films

Influence of copper species on silver grain size in Ag–CuO–SiO2 ternary nanocomposites

Effect of the Ag+ to Ag+/TiO2 film on the crystallization structure

Sol-Gel Preparation and Optical Properties of Ag Nanoparticle/TiO2 Composite Films

Effects of amines additives on the shapes of TiO2 nanoparticles

Formation of Silver Nano Particles in Percolative Ag‐PbTiO 3 Composite Dielectric Thin Film

Influence of Post-Annealing Treatment on the Morphology of Au Films Deposited on Liquid Surfaces

Crystallization and Optical Behaviour of Nanocomposite Sol-Gel TiO2:Ag Films

Preparation of Ag-Al2O3 nano-composites powder

Silver-Doping Induced Lattice Distortion in Tio2 Nanoparticles

Impacts of Two Alkanolamines on Crystallization and Morphology of Calcium Hydroxide

Effect of dispersed Ag on the dielectric properties of sol–gel derived PbTiO3 thin films on ITO/glass substrate

Effects of alkanolamine solvents on the aggregation states of reactive dyes in concentrated solutions and the properties of the solutions

Influence of Preparation Procedure on Physicochemical and Antibacterial Properties of Titanate Nanotubes Modified with Silver

Effect of Silver Nanoparticles on the Microstructure, Non-Isothermal Crystallization Behavior and Antibacterial Activity of Polyoxymethylene

SOL-GEL DERIVED BaTiO3 THIN FILMS WITH EMBEDDED SILVER NANOPARTICLES: PREPARATION AND DIELECTRIC PROPERTIES

The Effect of Dual Complexing Agents of Lactic and Citric Acids on the Formation of Sol-Gel Derived Ag–PbTiO3 Percolative Thin Film