Abstract:Determining the amine molecules behaviors in the nanochannels enables the interpretation of the microstructure and macroscopic properties of amines modified cement based materials. In this study, quantitative analysis were performed on the behaviors of amine molecules (TEPAs, PAMs and TEAs) by molecular dynamics (MD) simulation in the nanochannels of C-S-H gel. According to the interaction of amine molecules with C-S-H gel substrates or water molecules, research works revealed that amine molecules with special spatial structures illustrate different aggregation behaviors. TEPAs with linear structures tend to aggregate in a regular sequence at the center of the C-S-H gel nanochannels. Instead, PAMs and TEAs with branched structures prefer dispersing in the aqueous solution in the C-S-H gel nanochannels. Such different aggregation behaviors allow amine molecules to have various penetration depth and residence time in the interfacial regions. It was found that oxygen atoms and active hydrogen atoms in PAMs and TEAs can form stable interaction with calcium ions and oxygen atoms of C-S-H gel substrates, respectively. The oxygen involved bonds are stronger than nitrogen involved ones for all the molecules due to great electronegativity. There is no formation of hydrogen bonds in TEPAs, but polar atoms in PAMs and TEAs can interact through hydrogen bonding. Moreover, TEPAs cannot form strong hydrogen bonding with water molecules due to their aggregation behavior, whereas PAMs and TEAs formed strong hydrogen bonding with surrounding water molecules. In addition, formation of more hydrogen bonding with amine molecules leads to a lower diffusion coefficient of water molecules. Breakage of hydrogen bonds of water molecules causes the final failure of C-S-H/amine molecules nanocomposites subjected to tensile loads.

Impacts of Two Alkanolamines on Crystallization and Morphology of Calcium Hydroxide

A Comparative Study of the Effects of Two Alkanolamines on Cement Hydration

Microstructural characterization of cement in the presence of alkanolamines

Influence of Triethanolamine on the Hydration Product of Portlandite in Cement Paste and the Mechanism

Influences of Triethanolamine on the Performance of Cement Pastes Used in Slab Track

Influence of Triethanolamine on Elemental Concentrations in Aqueous Phase of Hydrating Cement Pastes

Towards a Further Understanding of Cement Hydration in the Presence of Triethanolamine

Formation of Synthetic C-S-H in the Presence of Triethanolamine And/or Polycarboxylate Polymers

Effect Of Potassium Sodium Tartrate And Sodium Citrate On The Preparation Of Alpha-Calcium Sulfate Hemihydrate From Flue Gas Desulfurization Gypsum In A Concentrated Electrolyte Solution

Influences of Citric Acid on the Metastability of Α-Calcium Sulfate Hemihydrate in CaCl2 Solution

Effects of Triethanolamine on Autogenous Shrinkage and Drying Shrinkage of Cement Mortar

Effects of Diethanolamine on the Evolution of Silver/titanium Dioxide Sol–gel Process

A Facile Method to Control the Structure and Morphology of Α-Calcium Sulfate Hemihydrate

Simultaneous effect of Na 2 EDTA on the phase transformation and morphology evolution during the transformation of gypsum into α -calcium sulfate hemihydrate

Trace NaCl and Na2EDTA Mediated Synthesis of Α-Calcium Sulfate Hemihydrate in Glycerol–Water Solution

Advances in understanding the effect of alkanolamine in cement-based materials

Impact of triethanolamine on the hydration of Portland cement in the presence of high pozzolanic activity supplementary cementitious materials

Effect of Diethanolisopropanolamine and Ethyldiisopropylamine on Hydration and Strength Development of Portland Cement

Influences of PCE Superplasticizers with Varied Architectures on the Formation and Morphology of Calcium Hydroxide Crystals

Effect of disodium EDTA on hydration and mechanical properties of calcium sulphoaluminate-belite cement

On the Characterization of Amine Molecules Behaviors in the Nanochannels Forming in Calcium Silicate Hydrate Gel