Formability of Ni/Al Micro-laminated Composite Sheet

Gong Pengtao,Lin Peng,Meng Lingjian,Huang Zhongsen,Cao Xiaoqing,Wang Tao
2022-01-01
Rare Metal Materials and Engineering
Abstract:The Ni/Al micro-laminated composite sheet was prepared by the vacuum hot pressing method. The mechanical properties and crack initiation and propagation laws of Ni/Al micro-laminated composite sheet were studied through uniaxial tensile experiments under different temperatures and different deformation degree. The results show that the Ni/Al micro-laminated composite sheet has poor plasticity from room temperature to 400 degrees C, and when the deformation is only 5%, the NiAl3 and Ni2Al3 intermetallic compound layer has produced more cracks perpendicular to the tensile direction. The Ni/Al micro-laminated composite sheet exhibits good plastic deformation ability at 600 degrees C, with the elongation at break as high as 56%, and when the deformation reaches 20%, the NiAl3 layer begins to appear microcracks, and the crack does not propagate to Ni2Al3 layer and Al layer when the deformation reaches 50%. The pressure free bulging experiment was used to study the forming performance of the Ni/Al micro-laminated composite sheet at 600 degrees C, and the microstructure distribution of the bulging part was characterized. The results show that the limit bulging rate (limit bulging height/die diameter) of Ni/Al micro-laminated composite sheet at 600 degrees C/5.5 MPa/8 min can reach 36.7%. The wall thickness of the gas bulged spherical shell gradually decreases from the bottom to the top, the top Ni and Al layers are severely necked, and cracks occur in the NiAl3 layer, but they do not extend to the Ni2Al3 layer and the Al layer.
What problem does this paper attempt to address?