Preparation and Conductivity of LSGM-(Li/Na)(2)CO3 Composite Electrolyte

Xu Shun,Lin Xuping,Ai Desheng,Peng Zhijian,Ge Ben

2018-01-01

Rare Metal Materials and Engineering

Abstract:Composite electrolyte made of La0.9Sr0.1Ga0.8Mg0.2O3-delta (LSGM) and a mixture of Li2CO3/Na2CO3 (48/52 at.%) was investigated with respect to their structure, morphology and ionic conductivity. Several proportions of polymethyl methacrylate (PMMA) was introduced during preparation of macro-porous LSGM matrices to create interconnected pore structures with different porosity factors that were found conducive for carbonate infiltration and integration with the membrane materials. Both mercury intrusion method and drainage method were used to investigate the porosity factor of LSGM matrixes. The structure and morphology of composite electrolyte were studied by SEM. The ac impedance method was used to test the ionic conductivity. Results show that the conductivity of the composite electrolytes increases with the increasing of proportions of PMMA after the melting point of carbonate and reaches 0.09 S/cm when the proportion of PMMA is 40 wt% at 600 degrees C. A watershed can be found from the Arrhenius plots [ln(sigma.T) vs T-1] of composite electrolytes at about 480 degrees C indicating the shift of the conduction mechanism caused by the melting of carbonate.