Coupling of tape casting and in situ solid-state reaction for manufacturing La0.9Sr0.1Ga0.8Mg0.2O3 electrolyte of efficient solid oxide cells

Changgen Lin,Yongmei Zhang,Jiaqi Qian,Zhiyi Chen,Jiongyuan Huang,Na Ai,San Ping Jiang,Xin Wang,Yanqun Shao,Kongfa Chen

DOI: https://doi.org/10.1016/j.jeurceramsoc.2024.01.059

IF: 5.7

2024-06-01

Journal of the European Ceramic Society

Abstract:Perovskite oxide La0.9Sr0.1Ga0.8Mg0.2O3 (LSGM) is an intermedium-temperature solid oxide cell electrolyte material with extraordinary oxygen-ion conductivity. However, the manufacturing procedures of LSGM discs are complex involving multiple steps of powder preparation, forming, and sintering at high temperatures. Herein, thin LSGM electrolyte discs are prepared by coupling of tape casting and in situ solid-state reaction using oxides/carbonates as the feedstock. A pure-phase LSGM electrolyte disc with uniform elemental distribution is obtained by sintering at 1450 °C, and it possesses an ionic conductivity of 0.105 S cm 1 at 800 °C, a thermal expansion coefficient of 12.2 × 10 6 K 1, and a bending strength of 156 MPa A 170 µm thick LSGM electrolyte-supported single cell delivers a peak power density of 0.96 W cm 2 at 800 °C and an electrolysis current density of 1.82 A cm 2 at 1.5 V with no noticeable degradation for 200 h. The findings of this research provide a cost-effective approach for manufacturing the LSGM electrolytes of efficient and durable solid oxide cells.

materials science, ceramics