Research on Oxidation Resistant ZrSi 2 –nbsi 2 Bilayer Coatings for an Nb–Ti–Si–Cr Based Ultrahigh Temperature Alloy

Xuan Li,Xiping Guo,Yanqiang Qiao

DOI: https://doi.org/10.1007/s11085-015-9564-1

IF: 2.2

2015-01-01

Oxidation of Metals

Abstract:Oxidation-resistant ZrSi 2 –NbSi 2 bilayer coatings were prepared on an Nb–Ti–Si–Cr based ultrahigh temperature alloy using a two-step (first sputtering Zr film, and then Si–Y co-deposition) process. The coatings prepared with different Zr film thicknesses possess a similar structure, consisting of a ZrSi 2 outer layer, a (Nb, X )Si 2 ( X represents Ti, Cr and Hf) middle layer and a (Ti,Nb) 5 Si 4 inner layer. The higher co-deposition temperature (Si–Y co-deposition at 1350 °C) would cause cracks at the interfaces between the constituent layers of the coatings. The coated specimens possess much lower mass gains than the base alloy after exposure of same static oxidation times at 1250 °C. After oxidation, a dense scale consisting of a mixture of SiO 2 , ZrSiO 4 , ZrO 2 , Al 2 O 3 , TiO 2 and Cr 2 O 3 formed, which could protect the specimen from oxidation at least for 100 h at 1250 °C in air.