Investigation on Preparation of Nb-Ti-Si-B Alloy Coatings with Siliconizing and Oxidation Resistance

Zhiping SUN,Yaxia GUO,Chongjun ZHAO
DOI: https://doi.org/10.14158/j.cnki.1001-3814.2016.12.043
2016-01-01
Abstract:The Si deposition coatings on Nb-18Ti-14Si-4.5B were prepared by pack cementation process,and the pack cementation process was processed at 1100 ℃ for 2.5 h,5 h,7.5 h and at 1200℃ for 5 h.The effects of B on the microstructure and formation mechanism of silicides coating were investigated.The oxidation resistance of typical coating after oxidating at 1250℃ for 20 h was studied.The results show that after oxidation,the coating has not fallen off,and NbSi2 coating is not totally consumed.The oxidation film of base alloy completely falls off.The mass gain of the base alloy is significantly higher than that of the coated alloy.