Abstract:Hot deformation behavior of the extruded Mg-6Gd-3Y (GW63) and Mg-6Gd-3Y-1Ag (GW63-1Ag) alloys was assessed by shear punch testing (SPT) method in the temperature range of 623 K to 723 K and shear strain rate of 1.6 × 10−2 to 1.3 × 10−1 s−1. Microstructural examinations showed that Ag addition decreased the initial grain size from 10.1 to 2.9 µm. According to the hot deformation results, hyperbolic-sine exponents (n-values) of 3.39 and 2.54 were obtained for the Ag-free and Ag-containing alloys, respectively. The corresponding activation energies were found to be 321 and 178 kJ mol−1 for these alloys. Therefore, the controlling deformation mechanisms were defined as viscous glide of dislocation for the Mg-6Gd-3Y alloy and grain boundary sliding for Mg-6Gd-3Y-1Ag. Processing maps were developed based on the dynamic material model (DMM) to determine the flow instability domains during hot deformation. Accordingly, the optimum hot working conditions were found to be in the temperature range of 655 K to 723 K and shear strain rate of 3.3 × 10−2 to 1.3 × 10−1 s−1 for the GW63-1Ag alloy, whereas the safe deformation window for the GW63 alloy was narrowed down to a temperature range of 665 K to 705 K and shear strain rate of 7.2 × 10−2 to 1.3 × 10−1 s−1. The Ag-containing alloy exhibited flow instability regions only at low temperatures and high strain rates. On the other hand, the Ag-free alloy demonstrated other instability domains comprising the formation of mechanical twins and cracking. Electron back-scattered diffraction analysis was utilized to correlate the microstructural evolution of the alloys after shear deformation to the hot working parameters. Continuous dynamic recrystallization was suggested as the main mechanism for generation of the dynamically recrystallized grains during hot deformation of both alloys.

Effects of Trace Ag on the Dynamic Recrystallization and Mechanical Properties of Mg-Gd-Y-Zr Alloy

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Effect of Gd content on microstructure and dynamic mechanical properties of solution-treated Mg−xGd−3Y−0.5Zr alloy

Hot compression behavior and microstructure evolution of Mg-Gd-Y-Zn-Zr alloy

Tuning texture and precipitation using Y/Gd atomic ratio in iso-concentration Mg–Y–Gd–Ag–Zr extruded alloys

Effect of Y and Gd solutes on grain refinement of the as-extruded Mg-Gd(-Y)-Zn-Mn alloys

Deformation-induced Dynamic Precipitation of 14H-LPSO Structure and Its Effect on Dynamic Recrystallization in Hot-Extruded Mg-Y-Zn Alloys

Effects of trace Zn on the deformation mechanisms of Mg‐Gd‐Y‐Zr alloy investigated by in‐situ synchrotron diffraction

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Unveiling the effect of Gd content on the dynamic recrystallization behavior and resultant mechanical property of magnesium

Effect of strain rate on dynamic recrystallization mechanism of Mg-Gd-Y-Sm-Zr alloy during hot compression

Effects of Mn, Zr on microstructure and properties of Mg-Gd-Y alloys

Effect of Ag Addition on the Hot Deformation, Constitutive Equations and Processing Maps of a Hot Extruded Mg-Gd-Y Alloy

Effect of Sn addition on the deformation behavior and microstructural evolution of Mg-Gd-Y-Zr alloy during hot compression

Enhanced age-hardening response and mechanical properties of the Mg-Gd-Y-Zn-Zr alloy by trace Ag addition

Dynamic Recrystallization Mechanism and Precipitation Behavior of Mg-6Gd-3Y-3Sm-0.5Zr Alloy During Hot Compression

Role of Y on the microstructure and mechanical properties of Mg-Gd-Zr alloy

Effect of Zn/(Gd+Y) ratio on the microstructure evolution and mechanical properties of Mg-Gd-Y-Zn-Zr alloy

Effect of Sm on dynamic recrystallization of Mg-8Gd-0.5Zr alloy during hot compression