Systematic investigations on the microstructural evolution and degradation mechanism of Cr 3 Si-coated Zry-4 under DBA and BDBA conditions
Haiyan Liao,Haibo Ruan,Weijiu Huang,Jin Hu,Xiangkong Xu,Xiaohan Deng,Junjun Wang,Yongyao Su
DOI: https://doi.org/10.1016/j.surfcoat.2024.131549
IF: 4.865
2024-11-22
Surface and Coatings Technology
Abstract:Cr 3 Si and Cr coatings were deposited on Zry-4 substrates via magnetron sputtering to examine their oxidation behavior in steam ranging from 1200 to 1400 °C. At 1200 °C, a dense Cr 2 O 3 layer that formed on the surface of the Cr 3 Si-coated Zry-4 followed a power-law function, preventing the internal diffusion of O. Additionally, an in-situ Zr 2 Si layer, developed between the Cr 3 Si coating and Zry-4 substrate, significantly mitigated the outward diffusion of Zr. However, at 1330 °C in steam, the continuity of the Zr 2 Si layer was disrupted due to the formation of ZrCr 2 , which facilitated the outward diffusion of Zr to the interface between the remaining Cr 3 Si layer and the outer Cr 2 O 3 layer. Despite the reduction in the Cr 2 O 3 layer thickness caused by redox reactions between Cr 2 O 3 and Zr, the Cr 3 Si coating still managed to delay the steam oxidation of the Zry-4 substrate for over 60 min at 1330 °C. While on the uncoated side, the thickness of the formed ZrO 2 reached 846 ± 5.2 μm. For the Cr coating, after 30 min of oxidation in steam at 1330 °C, a significant liquid eutectic formed between the Cr coating and the Zry-4 substrate, compromising the coating's overall structural stability. The oxidation resistance of the Cr 3 Si coating surpasses that of the Cr coating after exposure to steam at 1400 °C for 10 min. These findings suggest that the Cr 3 Si coatings hold promise for robustly protecting zirconium alloy cladding in scenarios involving design basis accidents (DBA) and beyond design basis accidents (BDBA).
physics, applied,materials science, coatings & films