Abstract:Cr 3 Si and Cr coatings were deposited on Zry-4 substrates via magnetron sputtering to examine their oxidation behavior in steam ranging from 1200 to 1400 °C. At 1200 °C, a dense Cr 2 O 3 layer that formed on the surface of the Cr 3 Si-coated Zry-4 followed a power-law function, preventing the internal diffusion of O. Additionally, an in-situ Zr 2 Si layer, developed between the Cr 3 Si coating and Zry-4 substrate, significantly mitigated the outward diffusion of Zr. However, at 1330 °C in steam, the continuity of the Zr 2 Si layer was disrupted due to the formation of ZrCr 2 , which facilitated the outward diffusion of Zr to the interface between the remaining Cr 3 Si layer and the outer Cr 2 O 3 layer. Despite the reduction in the Cr 2 O 3 layer thickness caused by redox reactions between Cr 2 O 3 and Zr, the Cr 3 Si coating still managed to delay the steam oxidation of the Zry-4 substrate for over 60 min at 1330 °C. While on the uncoated side, the thickness of the formed ZrO 2 reached 846 ± 5.2 μm. For the Cr coating, after 30 min of oxidation in steam at 1330 °C, a significant liquid eutectic formed between the Cr coating and the Zry-4 substrate, compromising the coating's overall structural stability. The oxidation resistance of the Cr 3 Si coating surpasses that of the Cr coating after exposure to steam at 1400 °C for 10 min. These findings suggest that the Cr 3 Si coatings hold promise for robustly protecting zirconium alloy cladding in scenarios involving design basis accidents (DBA) and beyond design basis accidents (BDBA).

Systematic Investigations on the Coating Degradation Mechanism During the Steam Oxidation of Cr-coated Zry-4 at 1200 °C

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Transient Experiments on Oxidation and Degradation of Cr-coated Zircaloy in Steam Up to 1600 ℃

Systematic investigations on the oxidation mechanism of Cr coated Zr-4 alloy under different high-temperature steam conditions

Steam oxidation of Cr-coated zirconium alloy claddings at 1200 °C: Kinetics transition and failure mechanism of Cr coatings

Steam Oxidation Of Cr-Coated Sn-Containing Zircaloy Solid Rod At 1000 Degrees C

Investigation of oxidation behaviors of bi-layer CrAl-Cr coated Zircaloy-4 in steam at 1300 oC

Isothermal Experiments on Eutectic and Oxidation Reactions of Cr-coated Zr Alloy Cladding in Steam at 1350 ℃: Behavior, Mechanism and Kinetics

Systematic investigations on the microstructural evolution and degradation mechanism of Cr 3 Si-coated Zry-4 under DBA and BDBA conditions

Temperature-time Dependence and Mechanisms of Redox Reaction in Cr-coated Zr Alloy Cladding During Steam Oxidation at 900-1250 ℃

Investigations on 1200 °C steam oxidation behavior of Cr coatings with distinct crystallographic orientation on Zircaloy-4 alloys

Evolution of Cr/Cr2O3 interface in Cr-coated zirconium alloy in high temperature steam

Isothermal experiments on steam oxidation of magnetron-sputtered chromium-coated zirconium alloy cladding at 1200 °C

Oxidation Behavior of Cr-coated Zirconium Alloy Cladding in High-Temperature Steam above 1200 °C

High-temperature steam oxidation behavior and failure mechanisms of Al alloyed Cr coatings on Zr-4 alloy

Steam oxidation of Cr-coated Sn-containing Zircaloy solid rod at 1000 °C

Degradation of the Cr 2 O 3 layer protectiveness caused by grain refinement during high-temperature oxidation of Cr coatings

Oxidation Behavior and Kinetics of Magnetron-sputtered Cr-coated Zr Alloy Cladding in 1000~1300°C Steam Environment

Growth kinetics and microstructure characteristics of the Zr-Cr interlayer in a Cr-coated Zry-4 alloy exposed to high-temperature steam

Investigation on Microstructures and High-Temperature Oxidation Resistance of Cr Coatings on Zircaloy-4 by Multi-Arc Ion Plating Technology

Oxidation behavior, thermal stability, and the coating/substrate interface evolution of CrN-coated Zircaloy under high-temperature steam