Abstract:At present, 5 G communication is developing rapidly, devices are becoming miniaturized, which requires the continuous emergence of materials with high dielectric constant. In this work, choosing Co2+ to sub-stitute Li1-2xCoxNb0.6Ti0.5O3 (LCNT, 0 <= x <= 0.1) + 0.4 wt% LBSCA ceramics successfully achieved high per-mittivity er and temperature stable resonant temperature frequency coefficient Tau f sintered at 950 degrees C, including er similar to 62, Qxf similar to 6255 GHz, and Tau f similar to 0.97 ppm/degrees C (x = 0.02), er similar to 56.55, Qxf similar to 7090 GHz, and Tau f similar to- 28.07 ppm/degrees C (x = 0.06). Meanwhile, the influence of Co2+ on LNT ceramics for phase composition, micro-structure, microwave dielectric performance and Raman vibration had been studied in detail. All samples belonged to M phase. Rod-like or blocky grains were gradually refined, indicating that Co2+ had the effect of grain refinement. In microwave dielectric performance, ionic polarizability played a leading role in er, Qxf value was positively correlated with the bulk density, Tau f directly depended on the average repeatable layer N. In Raman spectroscopy, three modes of Raman vibration had been identified as translation or rotation of Li+ ions, Nb/Ti bond vibration, [Nb/TiO6] octahedral vibration. To meet low temperature co-fired applications, the LCNT (x = 0.02) ceramic didn't react with Ag, which suggested it was achieving candidates for the next generation of medium K LTCC materials.(c) 2022 Elsevier B.V. All rights reserved.

Temperature-stable and Medium-High K of Ti/W Co-Doped M-phase LNT Microwave Ceramics for LTCC Dielectric Devices

Medium K and Temperature-Stable Co2+-substituted LiNb0.6Ti0.5O3 Microwave Dielectric Ceramics for LTCC Miniaturized Applications

Simultaneously achieving high permittivity and low loss in CuO/Nb2O5 substituted Li2O-TiO2-Nb2O5 low-temperature microwave dielectric ceramics

Li2WO4 Composite Ba3Ti4Nb4O21 Microwave Dielectric Ceramics with Near-Zero Temperature Coefficient and Low-Temperature Sintering for 5G Communication Devices

Low-Loss, Temperature-Stable, and Li-Enriched Li2.12ZnTi3O8 Dielectric Ceramics for LTCC Applications with V2O5 Addition

Enhanced the temperature stability of low-fired Li3Mg2NbO6 microwave dielectric ceramics for LTCC application

Temperature Stability of Low-Temperature Fired (1-X) ZnTiNb2O8-xCuTiNb2O8 Microwave Dielectric Ceramics

A New Microwave Dielectric Ceramic for LTCC Applications

Developing high performance, low temperature sintering and temperature stable K40 material in Co2O3/Nb2O5-modified Ba3Ti4Nb4O21 microwave dielectric ceramics for 5G-LTCC communication devices

Low Temperature Sintering and Microwave Dielectric Properties of Novel Temperature Stable Li3Mg2NbO6-0.1TiO2 Ceramics

A Novel Low‐permittivity LiAl0.98(Zn0.5Si0.5)0.02O2‐based Microwave Dielectric Ceramics for LTCC Application

Microwave Dielectric Properties of the Low-Temperature-fired Li2ZnTi3O8–Li2TiO3 Ceramics for LTCC Applications

Preparation and microwave dielectric properties of multilayer Li 1.075 Nb 0.625 Ti 0.45 O 3 co-fired ceramics with aqueous tape casting

Low-fired NiO-ZnO-TiO2-Nb2O5 Dielectric Ceramics with Temperature Stable for LTCC Applications

Low-temperature sintering and microwave dielectric properties of TiO<sub>2</sub>-based LTCC materials

Low-temperature sintering and microwave dielectric properties of TiO 2 -based LTCC materials

Microwave Dielectric Properties of Low-Fired Li2TiO3–MgO Ceramics for LTCC Applications

Microwave dielectric properties of the 5.5Li 2 O–Nb 2 O 5 –7TiO 2 ceramics

Li4Mg3Ti2O9: A novel low-loss microwave dielectric ceramic for LTCC applications

Temperature stable Li5.5Nb1.5O6F-based microwave dielectric ceramics for LTCC applications

Low-fired Li3Mg2NbO6 microwave dielectric ceramics by adding LMBCS glass for LTCC application