Abstract:This work presents the results of research on the influence of the amount of p-toluenesulfonic acid and phosphoric acid (V) added to the phenol-formaldehyde resin (pH 7.3–7.8) on its thermal properties and on the phenol-formaldehyde-carbon composite produced on its basis. This material undergoes pyrolysis under high temperature. The addition of a catalyst to the phenol-formaldehyde resin affects its curing rate and degree of cross-linking, but how it affects the thermal properties of the resin depending on the temperature is the subject of this work. This article presents the results of thermal tests for phenol-formaldehyde resin and phenol-formaldehyde-carbon composite. It was examined how the content of the catalyst used during the production process affects the individual thermal parameters of the mentioned materials. The results include experimental tests of thermal diffusivity with uncertainty (±3%), specific heat capacity (±2.5%), thermal expansion with resolution 2 nm analyzed in the temperature range −40–115 °C and thermogravimetric TG/DTA analysis with resolution 0.03 μg in the temperature range from room temperature (RT = 23 °C) to 550 °C. Individual thermal tests showed changes in the thermal properties caused by changes in the catalyst content of the tested materials and the influence of the addition of carbon fibers on the properties of the composite compared to the pure phenol-formaldehyde resin. It was found that there is a certain maximum level of catalyst weight fraction at which the greatest decrease in thermal diffusivity occurs. In the case of phenolic-formaldehyde-carbon composite at −40 °C, an increase in catalyst weight fraction from 2 to 4 wt% caused a decrease in thermal diffusivity by 18.2%, and for phenol-formaldehyde resin, it was 2.8% with an increase in catalyst fraction from 4 to 10 wt%.

Ferrocenecarboxaldehyde Modified Terephthalaldehyde-Phenolic Resin: A Comprehensive Study on the Synthesis, Curing Behavior, and Pyrolysis Process

Synthesis, Curing, and Thermal Stability of Low-Temperature-Cured Benzoxazine Resins Based on Natural Renewable Resources

In-situ Synthesis of Ferrocene Modified Formaldehyde-Free Phenolic Resin and Its Temperature-Resistant Microwave Absorbing Coating

Curing and pyrolysis behavior of PF/B4C/PBZ composite

Preparation and Characterization of Porous Carbons Obtained from Mixtures of Furfuryl Alcohol and Phenol-Formaldehyde Resin

Influence of Poly (dihydroxybiphenyl Borate) on the Curing Behaviour and Thermal Pyrolysis Mechanism of Phenolic Resin

Structural and Thermal Behavior of a Novel Phenolic Resin and Its Composite with Excellent Ablative Performance

From Self-Organized Novolac Resins to Ordered Nanoporous Carbons

Synthesis and characterization of fluorine-containing polyester based on phthalic anhydride and tetrafluoropropyl glycidyl ether

Optimization of Crosslinked Network Structure of Cured Phenolic Resin with High Char Yield

Pyrolysis kinetics of tannin–phenol–formaldehyde resin by non-isothermal thermogravimetric analysis

The Effect of p-Toluenesulfonic Acid and Phosphoric Acid (V) Content on the Heat Resistance and Thermal Properties of Phenol Resin and Phenol-Carbon Composite

Study on the Curing Behavior of Polythiol/phenolic/epoxy Resin and the Mechanical and Thermal Properties of the Composites

A tough, strong, and fast-curing phenolic resin enabled by dopamine-grafted chitosan and polyethyleneimine-functionalized graphene

Modified Phenolic Resin with Aluminium and Rectorite: Structure, Characterization, and Performance

Effect of addition of comonomer FDCA on thermal, mechanical, and crystallization properties of bio-based semi-aromatic PA10T

Effect of Grafted Polytetrafluoroethylene Nanoparticles on the Mechanical and Tribological Performances of Phenol Resin

Microstructure and properties of resin-based pyrocarbon with micro-nano structure carbon and TiO2 as additives

Synthesis, Characterization, and Thermal Pyrolysis Mechanism of Resorcinol‐Formaldehyde Resin‐Containing Phenylboronic Acid

Study on improving the high-temperature oxidation resistance of pyrolytic carbons of phenolic resin binder by in-situ formation of carbon nanotubes

Mesoporous Carbons from Nanostructured Phenolic Thermosets Containing Poly(Styrene-Alt-Maleic Anhydride)-Block-Polystyrene Diblock Copolymer