Abstract:Epoxy resin carbons are of high strength, high temperature resistance, and corrosion resistance, which are widely used as the precursor of carbon composite materials. However, the applications of epoxy resin carbons are greatly limited for the characteristic of non-graphitization and low char yield (22 wt%). In this paper, coal tar pitch was used to modify epoxy resin carbons via a simple heating mixing, pyrolysis and high temperature graphitization. The results show that the coal tar pitch content and heat treatment temperature can improve the ordered graphite carbon content. As the coal tar pitch content increase, the ordered graphite carbon content of modified epoxy resin carbon increase after 3000 °C graphitization for 0.5 h. Particularly, the graphitization degree of epoxy resin carbon and 40 wt% coal tar pitch modified epoxy resin carbon are 8.42 % and 44.21 %, respectively. The grain size (L c = 13.84 nm) and grain stacking height (L a = 7.79 nm) of 40 wt% coal tar pitch modified epoxy resin carbon are bigger than epoxy resin carbon (L c = 3.44 nm, L a = 3.45 nm). The ordered coal tar pitch graphite carbon and disordered epoxy resin amorphous carbon are evenly distributed in the modified epoxy resin carbon, indicating a good comparability of coal tar pitch and epoxy resin. Besides, the entangling carbon ribbon are observed in the epoxy resin carbon after graphitization at 3000 °C. With the increase of coal tar pitch content, the content of carbon element, aromatic ring number, the char yield and thermal decomposition temperature of modified epoxy resin increased. Moreover, the char yield of expoxy resion modified by 50 wt% coal tar pitch is 42 wt%, almost two times higher than that of epoxy resin (22 wt%). The increased char yield of modified epoxy resin mainly inherited the high char yield of coal tar pitch (50 wt%) and the chemical crosslinking weight gain. More interesting, the chemical crosslinking weight gain reaches the maximum value of 15 wt% when the content of coal tar pitch is 40wt%. The reason for that is the possible chemical crosslinking reaction can be occured by the epoxy group and hydroxyl group within epoxy resin and carboxyl group and phenolic hydroxyl group within coal tar pitch. This study provides some theory foundation for the future application of epoxy resin carbon composite materials.

Microstructure and properties of resin-based pyrocarbon with micro-nano structure carbon and TiO2 as additives

Study on improving the high-temperature oxidation resistance of pyrolytic carbons of phenolic resin binder by in-situ formation of carbon nanotubes

Improved Thermal Stabilities, Ablation and Mechanical Properties for Carbon Fibers/Phenolic Resins Laminated Composites Modified by Silicon-containing Polyborazine

Investigation of the mechanical and flame retardant properties of carbon fiber modified phenolic epoxy resin

Ferrocenecarboxaldehyde Modified Terephthalaldehyde-Phenolic Resin: A Comprehensive Study on the Synthesis, Curing Behavior, and Pyrolysis Process

High temperature flexural strength, microstructure, phase evolution and anti-oxidation mechanism of Al-coated carbon fiber/boron phenolic resin ceramizable composite modified with TiB2 and B4C

Effect of coal tar pitch modification on the structure and char yield of pyrolysis epoxy resin carbons

Microstructure, Mechanical Property and Thermal Conductivity of Porous TiCO Ceramic Fabricated by In Situ Carbothermal Reduction of Phenolic Resin and Titania

Curing and pyrolysis behavior of PF/B4C/PBZ composite

Fabrication and Characterization of TiO2 Nanotube–Epoxy Nanocomposites

Low-temperature oxidation behavior of the isotropic pyrocarbons

Pyrolysis mechanism and combustion behaviors of high impact polystyrene improved by modified ammonium polyphosphate and graphene

Pyrolysis behavior of the nanoporous phenolic matrix and the resultant microstructure and property evolution in the composites

Structural and Thermal Behavior of a Novel Phenolic Resin and Its Composite with Excellent Ablative Performance

Reinforcement of C/C materials prepregs with pyrocarbon coated carbon fiber as the way to improve the prepregs properties after pyrolysis

The effect of carbon nanotubes/NiFe2O4 on the thermal stability, combustion behavior and mechanical properties of unsaturated polyester resin

Combustion Inhibition Ability of Piperazine Phosphoramide Derivatives and Titanium Carbide on Epoxy Resin

Fabrication and characterization of pyrolytic carbons from phenolic resin reinforced by SiC nanowires with chain-bead structures

Influence of Poly (dihydroxybiphenyl Borate) on the Curing Behaviour and Thermal Pyrolysis Mechanism of Phenolic Resin

Effect of Pyrocarbon Content in C/C Preforms on Microstructure and Mechanical Properties of the C/C–SiC Composites

Oxidation resistance, ablation resistance and in situ ceramization mechanism of Al-coated carbon fiber/boron phenolic resin ceramizable composites modified with Ti3SiC2