Abstract:The requirements for long-term stability and thermal performance of resin-based coating materials are gradually increasing with the development of aerospace industry. As a low-toxicity aldehyde, terephthalaldehyde (TPA) with aromatic ring structure and high reactivity is an ideal formaldehyde substitute for synthesizing high thermal stability phenolic resins and coating candidate. In this work we provided a strategy for the synthesis of ferrocenecarboxaldehyde (Fc) in-situ modified TPA-phenol resin (PTPA-Fc), obtaining resin products with high glass transition temperatures at 302 degrees C. The non-isothermal curing process and activation energy changes of resins with different TPA-phenol ratios were further investigated. It was found that the highest cross-linking density of resin was achieved when TPA/phenol was 0.5, with the initial decomposition temperature (T-5%) reached 378 degrees C. Afterwards, carbonyl iron powder (CIP) filled PTPA-Fc microwave absorbing coating was prepared. Due to the improved oxidation resistance, composite based on PTPA-Fc had an effective bandwidth of 3.1 GHz (14.5-17.6 GHz, thickness 3 mm) after 100 h heat treatment at 250 degrees C and could still cover the 9.5-18 GHz absorption band (with RL <= -5 dB) with 5 mm matching thickness, reflecting a good long-term thermal stability.

In-situ Synthesis of Ferrocene Modified Formaldehyde-Free Phenolic Resin and Its Temperature-Resistant Microwave Absorbing Coating