Abstract:There is a potential for leveraging the synergy of carbonationof portlandite and Mg-based binders to improve the CO2 uptake,mechanical property, and thermodynamic stability of Mg- and Ca-basedbinders and enable its application. This work reports insights intothe carbonation behavior of Mg(OH)(2)-Ca(OH)(2) (MH-CH) mixtures including the precipitation of differentcarbonates, degree of reaction of each phase, mechanical properties,microstructure characterization, and thermodynamic stability. Resultsindicate that the compressive strength and degree of carbonation (DOC)of compacts increase first and then decrease with the increase ofthe Ca(OH)(2) content. The compact containing 25% Ca(OH)(2) yields the highest compressive strength of 91.4 MPa, whilethe compact containing 75% Ca(OH)(2) has the highest DOCof 91.2%. The formation of nesquehonite with a lower density in compactswith lower contents of Ca(OH)(2) (0 and 25%) results in ahigher volume increase even at a very low DOC (14.2%), leading toa more densified structure in the compacts. Compacts with higher contentsof Ca(OH)(2) (50, 75, and 100%) precipitate calcite and magnesiumcalcite with higher thermodynamic stability than nesquehonite andimproved water stability. Meanwhile, the high temperature in the initialstage of Ca(OH)(2) carbonation causes severe water evaporationand insufficient water in compacts, thus restricting the continuouscarbonation at the center having a lower DOC than the surface. Themixing of Mg(OH)(2) and Ca(OH)(2) significantlyenhances the carbonation degree of both hydroxides, which may be explainedby the complementation of Ca(OH)(2) and Mg(OH)(2) carbonation, in which the water released by the carbonation of Ca(OH)(2) is bound to the crystal structure of hydrated magnesium carbonates(HMCs) from Mg(OH)(2) carbonation. This work reports insights into the carbonationbehaviorof Mg(OH)(2)-Ca(OH)(2) mixtures, which havebeen proposed to be sustainable binders as potential CO2 sinkers.

Elucidating the Interaction Mechanism of Mg(OH)<sub>2</sub> and Ca(OH)<sub>2</sub> under Enforced Carbonation

Influence of Magnesium Hydroxide Content and Fineness on the Carbonation of Calcium Hydroxide

Enhancing the Carbonation of Γ-C2s Through MgCl2 Incorporation

Novel Carbonated Materials: the Synergistic Role of MgO in Partially Calcined Limestone

Thermodynamical Analysis of the Effects of Modifiers and Carbonation on the Phase Assemblages of Magnesium Oxychloride Cement

Exploring Mechanisms of Hydration and Carbonation of MgO and Mg(OH)2 in Reactive Magnesium Oxide-based Cements

Comparative Study on the Carbonation-Activated Calcium Silicates As Sustainable Binders: Reactivity, Mechanical Performance, and Microstructure

Effect of Hydrated Magnesium Carbonate Grown in Situ on the Property of MgO-activated Reactive SiO2 Mortars

Effects of Citrate Acid, Solidum Silicate and Their Compound on the Properties of Magnesium Oxysulfate Cement under Carbonation Condition

Influence of Mole Ratio of Calcium to Magnesium on Carbonation Properties of Calcium Hydroxide

Compaction and Mechanical Characteristics and Stabilization Mechanism of Carbonated Reactive MgO-stabilized Silt

Characterization of the Interfacial Transition Zone in Carbonated Low-Calcium Co2 Sequestration Binder Mortar

Enhancing Aqueous Carbonation Via Co-Milled Serpentine and Wollastonite: Effects of Mechanochemical Activation

Magnesium silicate hydrate (M-S-H) stability under carbonation

Hydration, carbonation and strength development of reactive MgO cement blended with lime (CaO) under different curing conditions

Preparation of calcium carbonate binders via CO2 activation of magnesium slag

Experimental investigation into the self-carbonation mechanism of magnesium oxide carbon sequestration foamed concrete

Effect of MgO content on the quantitative role of hydrotalcite-like phase in a cement-slag system during carbonation

MgO activated calcined marine clay and its carbonation

Carbonation behavior of calcium silicate hydrate (C-S-H): Its potential for CO2 capture

Reaction Mechanism of Ca(OH)2-based Carbon Storage Suitable for the Production of Building Materials