Abstract:Calcium silicate hydrate (C-S-H), as the main component of cementitious materials, is susceptible to carbonation presenting a potential to capture CO2. Although some researches paid attentions to the carbonation behaviors of C-S-H given the durability of concrete structure, the kinetics of C-S-H carbonation as well as changes of C-S-H itself under carbonation have not been fully addressed. In this study, the carbonation kinetics of C-S-H with various calcium to silica ratio (Ca/Si) were investigated and the evolution of carbonation products in terms of compositions and micro-mechanical properties was quantitatively characterized by quantitative X-ray diffraction (QXRD), energy dispersive spectroscopy (EDS), and nuclear magnetic resonance (NMR). Three distinct periods are found in the course of C-S-H carbonation, encompassing dissolution period, diffusion period and slowly ongoing reaction period. A progressive decrease in Ca/Si and pH is observed in dissolution period with the formation of calcium carbonate, the reaction rate of which is strongly dependent on the initial Ca/Si of C-S-H. In the diffusion period, a small proportion of crosslinking occurs in C-S-H structure before producing a large amount of calcium modified silica gel, during when the Ca/Si and pH remain unchanged due to the incongruent dissolution of C-S-H as revealed by thermodynamic modellings. In the slowly ongoing reaction period, C-S-H decomposed completely and the mixture of microcrystalline calcium carbonate and calcium modified silica gel becomes the final product. The micro-mechanical property of C-S-H was significantly weakened by the change of phase assemblage. Our findings do not only advance our understandings on the deterioration of cementitious material under carbonation but also provides new insights into the CO2 capture using C-S-H widely existing in cementitious materials.

Magnesium silicate hydrate (M-S-H) stability under carbonation

Dissolution kinetics of cementitious magnesium silicate hydrate in air‐equilibrated water

Properties of magnesium silicate hydrates (M-S-H)

Effects of Ca/Si Ratio, Aluminum and Magnesium on the Carbonation Behavior of Calcium Silicate Hydrate

Carbonation behavior of calcium silicate hydrate (C-S-H): Its potential for CO2 capture

Exploring Mechanisms of Hydration and Carbonation of MgO and Mg(OH)2 in Reactive Magnesium Oxide-based Cements

The physiochemical alterations of calcium silicate hydrate (C-S-H) under magnesium attack

A critical review of magnesium silicate hydrate (M-S-H) phases for binder applications

Polymorphism and Phase Stability of Hydrated Magnesium Carbonate Nesquehonite MgCO3·3H2O: Negative Axial Compressibility and Thermal Expansion in a Cementitious Material

Effect of MgO content on the quantitative role of hydrotalcite-like phase in a cement-slag system during carbonation

Cementitious and hardening properties of magnesia (MgO) under ambient curing conditions

Study on the Stability of Low-Carbon Magnesium Cementitious Materials in Sulfate Erosion Environments

Effect of carbonation on calcium silicate hydrate

Dense Hydrated Magnesium Carbonate MgCO3·3H2O Phases

Durability of Magnesium Oxychloride Cement in Application: Phase Composition Transition and Microstructure Characteristics

Temperature-dependent rehydration of magnesium silicate hydrate (M-S-H): Development of no-cement binder through MD/DFT validation

Mechanical Properties, Microstructure, and Mechanism of Nanosilica-Modified Low-Carbon Magnesium Silicate Hydrate Cement

Experimental investigation into the self-carbonation mechanism of magnesium oxide carbon sequestration foamed concrete

M- S-H formation in MgO-SiO2slurries via wet milling for magnesia based castables

Thermodynamic study on the phase assemblage of MPC exposed to natural and accelerated carbonation conditions

Effect of MgO and superfine slag modification on the carbonation resistance of phosphogypsum-based cementitious materials: Based on hydration enhancement and phase evolution regulation