Abstract:The carbonation behavior of calcium-containing sorbents, CaO and Ca(OH)2, was investigated under pressurized CO2 at nominal room temperature. The carbonation reaction was mechanically driven via reactive ball milling. The carbonation rate was determined by monitoring the CO2 pressure inside the sealed milling jar. Two different versions of CaO were fabricated as starting materials. The addition of citric acid in CaO synthesis resulted in a significant increase in sorbent surface area, bringing up the conversion of CO2 from 18% to 41% after 3 h of reactive milling. The hydroxide formation from these two oxides closed the surface area gap. Nevertheless, we found that hydroxides had a higher initial carbonation rate and greater final CO2 uptake than their oxide counterparts. However, the formation of byproduct water limited the further carbonation of Ca(OH)2. When we added a controlled amount of water to the CaO-containing milling jar, the highest carbonation rate and most extensive CO2 uptake were attained due to the in situ formation of reactive Ca(OH)2 nanoparticles. We saw CaCO3 X-ray diffraction peaks only when Ca(OH)2 was involved in this low-temperature carbonation, indicating that the grain growth of CaCO3 is easier on the Ca(OH)2 surface than on the CaO surface. We used the Friedman isoconversional method to calculate the effective activation energy of decarbonation for the high surface area CaO sorbent milled with water. The average effective activation energy was found to be about 72 kJ mol−1, and its magnitude started to decrease significantly from 50% sorbent regeneration. The drastic change of the effective activation energy during decarbonation suggests that CaCO3, formed at nominal room temperature by reactive milling under pressurized CO2, should undergo a more drastic morphology change than the typical thermally carbonated CaCO3.

Influence of Mole Ratio of Calcium to Magnesium on Carbonation Properties of Calcium Hydroxide

Influence of Magnesium Hydroxide Content and Fineness on the Carbonation of Calcium Hydroxide

Modulation of nano CaCO3pore size and effect on properties of carbonation reaction

Effects of Ca/Si Ratio, Aluminum and Magnesium on the Carbonation Behavior of Calcium Silicate Hydrate

Influences of Molding Pressure on Products Morphology and Carbonated Efficiency of Calcium Hydroxide

Thermodynamical Analysis of the Effects of Modifiers and Carbonation on the Phase Assemblages of Magnesium Oxychloride Cement

Influence of Compaction Pressure on the Accelerated Carbonation of Calcium Hydroxide

Effect of Hydrated Magnesium Carbonate Grown in Situ on the Property of MgO-activated Reactive SiO2 Mortars

Effect of MgO content on the quantitative role of hydrotalcite-like phase in a cement-slag system during carbonation

Magnesium silicate hydrate (M-S-H) stability under carbonation

Compaction and Mechanical Characteristics and Stabilization Mechanism of Carbonated Reactive MgO-stabilized Silt

Aqueous Carbonation of MgSO4 with (NH4)(2)CO3 for CO2 Sequestration

Comparative experiments on carbonated silts treated by magnesia with different activity

Experimental Study and Modeling of Cao Carbonation: Effects of Operating Conditions on the Carbonation Behaviors of the Calcined Limestone Particles

Property Changes of Reactive Magnesia-Stabilized Soil Subjected to Forced Carbonation

Effects of Citrate Acid, Solidum Silicate and Their Compound on the Properties of Magnesium Oxysulfate Cement under Carbonation Condition

Calcium-Based Sorbent Carbonation at Low Temperature via Reactive Milling under CO2

Hydration, carbonation and strength development of reactive MgO cement blended with lime (CaO) under different curing conditions

Effects of CO2 Concentration and the Uptake on Carbonation of Cement-Based Materials

Assessment Method of Carbonation Degree and Activity of a Wide Range of Calcium/magnesium Containing Solids

Hydraulic Conductivity Characteristics of Carbonated Reactive Magnesia-Treated Silt