Abstract:Magnetostrictive alloys with a wide operating temperature range from −80 to 150°C were developed by changing the Tb/Dy ratio of TbxDy1−xFe2 from 0.3/0.7 to 0.36/0.64 and Co partly substituting for Fe. The structure, Curie temperature, AC susceptibility, magnetization, magnetocrystalline anisotropy constant K1 and magnetostriction of Tb0.36Dy0.64(Fe1−yCoy)2 (y=0.0, 0.1, 0.2) alloys were investigated. It was found that the matrix of Tb0.36Dy0.64(Fe1−yCoy)2 alloys keeps the MgCu2-type cubic Laves structure with a small amount of R-rich phase. A small amount of R2(Fe,Co) phase was also detected when y=0.2. The Curie temperature Tc of Tb0.36Dy0.64(Fe1−yCoy)2 alloys is higher than Tb0.3Dy0.7Fe2 and increases drastically with increasing Co content from 387.1°C for Tb0.36Dy0.64Fe2 to 416.7°C for Tb0.36Dy0.64(Fe0.9Co0.1)2 and 433.3°C for Tb0.36Dy0.64(Fe0.8Co0.2)2. The spin reorientation temperature Tr decreases from −12°C for Tb0.3Dy0.7Fe2 to −94°C for Tb0.36Dy0.64Fe2. It increases slightly with increasing Co content. The magnetocrystalline anisotropy coefficient K1 of Tb0.36Dy0.64(Fe1−yCoy)2 alloys is greater than Tb0.3Dy0.7Fe2 but decreases with increasing Co content. The saturation magnetization Ms of Co-doped alloys is lower than that of Tb0.3Dy0.7Fe2 and decreases with increasing Co content. The magnetostriction of Tb0.3Dy0.7Fe2 and Tb0.36Dy0.64(Fe1−yCoy)2 alloys was examined against applied magnetic field up to 5kOe in the temperature range from −80 to 150°C.The temperature coefficient of magnetostriction (Δλ/ΔT) of Tb0.3Dy0.7Fe2 and Tb0.36Dy0.64(Fe1−yCoy)2 alloys was also calculated by linearly simulating the magnetostriction-temperature curve, showing that the absolute value of Δλ/ΔT at 5kOe magnetic field is 1.17 ppm/°C for y=0.1 and 1.35 ppm/°C for y=0.2, smaller than that of Co free samples, which is 2.43ppm/°C for Tb0.36Dy0.64Fe2.

Large Magnetostriction of Nd0.2Tb0.3Dy0.5Fe1.93/epoxy Composites in a Wide Temperature Range

Magnetostriction and electrical resistivity of Sm0.88Nd0.12Fe1.93 bonded composites

Large magnetostriction over a wide temperature range in a Nd0.2TbxDy0.8−xFe1.93 Laves compound

Design and Large Magnetostriction of Tb0.34Dy0.56Pr0.1Fe1.9/epoxy Composite Containing Near-Spherical Single-Crystal Particles

Giant Magnetostriction in TbDyFe/epoxy Composites with Spherical Single-Crystal Particles

Effects of manganese substitution on magnetic and magnetostrictive properties of Tb0.5Dy0.5(Fe1-xMnx)1.92/epoxy composites with spherical single-crystal particles*

Structure and magnetic properties of mechanically alloyed Tb0.7Pr0.3(Fe0.9B0.1)1.93 and the magnetostriction of its epoxy composites

Exceptional combination of large magnetostriction, low hysteresis and wide working temperature range in (1-x)TbFe2-xDyCo2 alloys

Magnetostriction of Tb0.36Dy0.64(Fe1−xCox)2 (x=0–0.20) 〈112〉-oriented crystals

Fabrication of Tb0.3Dy0.7Fe2/epoxy composites: Enhanced uniform magnetostrictive and mechanical properties using a dryprocess

Magnetomechanical Behaviors of Giant Magneto Strictive Materials

A Kind of Wide Operating Temperature Range Giant Magnetostrictive Alloys

The Co-Doped Tb0.36dy0.64fe2 Magnetostrictive Alloys with A Wide Operating Temperature Range

Optimization On Magnetic Transitions And Magnetostriction In Tbxdyyndz(Fe0.9co0.1)(1.93) Compounds

Magnetostriction of 〈110〉 Oriented Crystals in Tb0.36Dy0.64(Fe1−xCox)2 (x = 0–0.30) Alloys

Magnetostriction of a (110) oriented Tb0.3Dy0.7Fe1.95 polycrystals annealed under a noncoaxial magnetic field

Preparation of Terfenol-D Spherical Single-Crystal Particles and Study of Magnetostrictive Properties of Its Composites at Low Fields

Solid-state Synthesis and High Magnetostriction Performances of Heavy Rare Earth–Free Sm0.88Nd0.12Fex Particulate Composites

Mechanical and Magnetostrictive Properties of Tb0.36dy0.64(Fe1-Xmnx)(1.9) Alloys

Anisotropic magnetostriction for Tb0.3Dy0.7Fe1.95 alloys under magnetomechanical loading

Magnetomechanical damping capacity of (110) oriented Tb0.36Dy0.64 (Fe0.85Co0.15)2 alloy