Abstract:Fe81Al19Tb x (x = 0, 0.05, 0.1, 0.2, 0.3, 0.4) alloys were prepared by a non-consumable vacuum arc melting technique under an inert argon gas atmosphere. The microstructures of the alloys were studied by X-ray diffraction (XRD) and scanning electron microscopy combined with an energy dispersive spectroscopy (SEM/EDS). The magnetic properties and magnetostriction coefficients of the alloys were measured by a vibrating sample magnetometer (VSM) and adifferential resistive strain sensor, respectively. The results show that the Fe81Al19 alloy consists of a single A2 phase with bcc structure, whereas the Tb doped Fe81Al19 alloys are composed of the A2 phase and a small amount of rare earth-rich phase. The doping of the rare earth element Tb makes the Fe81Al19 alloy preferentially oriented along with the <100> crystal direction. With the increase of Tb content, the magnetostriction coefficient of the alloy first increases and then decreases. When x=0.1, the magnetostriction coefficient reaches the maximum, which is 146 × 10−6. Compared with the as-cast Fe81Al19 alloy (27 × 10−6), it increases by 441%. The enhanced magnetostrictive properties are mainly attributed to the preferred orientation along <100> of A2 phase of the Tb doped Fe81Al19 alloys and lattice distortion caused by the small amount of rare earth atoms entering the Fe–Al alloy lattice.

Structure and magnetic properties of mechanically alloyed Tb0.7Pr0.3(Fe0.9B0.1)1.93 and the magnetostriction of its epoxy composites

Magnetostriction and electrical resistivity of Sm0.88Nd0.12Fe1.93 bonded composites

Synthesis and magnetostriction of TbxPr1−x(Fe0.8Co0.2)1.9 cubic Laves alloys

High Pr-content (Tb0.2Pr0.8)(Fe0.4Co0.6)1.93−xBx magnetostrictive alloys

Synthesis and Magnetostriction of Melt-Spun Pr1−xTbx(Fe0.6Co0.4)2 Alloys

Design and Large Magnetostriction of Tb0.34Dy0.56Pr0.1Fe1.9/epoxy Composite Containing Near-Spherical Single-Crystal Particles

Structure and Magnetostriction of Dy 0.9-X Tb X Pr 0.1 Fe 1.85 and Dy 0.9-X Tb X Pr 0.1 (fe 0.95 Al 0.05 ) 1.8 Alloys

Structure and magnetostriction of Tb0.4Nd0.6(Fe0.8Co0.2)1.90 alloy prepared by solid-state synthesis

High-pressure Synthesis of Giant Magnetostrictive PrxTb1−xFe1.9 Alloys

Magnetics, Magetostriction, and Spin Reorientation of Tb0.3dy0.6pr0.1(Fe1-Xalx)(1.95) Alloys with Substitution of Fe by Al

Microstructure and Magnetostriction of (dy0.7tb0.3)1−xprxfe1.85 and (dy0.7tb0.3)0.7pr0.3fey Alloys

Structure and magnetostriction of Tb0.36Dy0.64(Fe0.85 Co0.15)2-xBx alloys

Magnetostriction of Dy0.6Tb0.3Pr0.1(Fe0.95Mn0.05)x Alloys (1.80 ≤ × ≤ 1.95)

Synthesis and Magnetostrictive Properties of Pr(Fe1.95b0.05)(1.93) Bulk Nanocrystalline Alloy

Synthesis and Magnetic Properties of Pr(Fe 1-X Co X ) 2 and Pr 1-Y Tb Y (fe 0.4 Co 0.6 ) 2 Alloys

Influence of rare earth element terbium doping on microstructure and magnetostrictive properties of Fe81Al19 alloy

Structure and Magnetostriction of (dy0.6tb0.3pr0.1)(fe0.95−xmn0.05gax)1.85 Alloys

Magnetism， Magetostriction， and M?ssbauer Effect Studies of Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 Alloys

Effects of manganese substitution on magnetic and magnetostrictive properties of Tb0.5Dy0.5(Fe1-xMnx)1.92/epoxy composites with spherical single-crystal particles*

Synthesis and Magnetostrictive Properties of High-Pr Content ${\rm Sm}_{1-x}{\rm Pr}_{x}{\rm Fe}_{1.9}$ Cubic Laves Alloys

Structure and Magnetostriction of Grain-Oriented Dy_(0.6) Tb_(0.3) Pr_(0.1) (fe_(0.95) Mn_(0.05) )_x Alloys