High cycle fatigue behavior and fatigue life extension mechanism of laser shock peened metal matrix composites

CAO Zi-wen,SUN Ru-jian,CHE Zhi-gang,WU Jun-feng,ZOU Shi-kun

DOI: https://doi.org/10.3969/j.issn.1007-2012.2023.04.019

2023-01-01

Abstract:To improve the high cycle fatigue performance of metal matrix composites, the laser shock peened surface modification of SiC particles reinforced 2009 aluminum matrix composites（SiCp/2009Al） was used to investigate the high cycle fatigue life of three-point bending, and the evolution laws of residual stress, microhardness, surface morphology and microstructure during laser shock process were revealed. The results show that the high cycle fatigue life of laser shock peened SiCp/2009Al with laser energy of 10,20 and 30 J is significantly improved by 131%, 259% and 182%, respectively, and the corresponding surface residual stress is-127.3,-156.0 and-168.3 MPa, respectively. Laser shock induces deformation pits with depth of about 30 μm on the surface of SiCp/2009Al, the surface microhardness increases from 160 HV of the base metal to 180 HV, and a large number of high density dislocation structures appear. The residual compressive stress and microhardness of metal matrix composite surface are increased obviously, and the increase of fatigue life extension is considerable.