Effect of 3D Printing Process Parameters on Mechanical Properties of TPU Samples

Xierenguli Maitituersun,Li Nan,Wurikaixi Aiyiti

DOI: https://doi.org/10.3969/j.issn.1009-9492.2023.03.005

2023-01-01

Abstract:Thermoplastic polyurethane（TPU）, as a kind of polymer material with high elasticity and good mechanical properties, has been widely used in industry and clothing and other fields. 3D printing technology further expands the application of TPU materials in these fields.However, the 3D printing process parameters have certain influence on the mechanical properties of TPU materials. Therefore, the TPU wire with diameter of 1.75 mm was selected as the test material to conduct the mechanical tensile test of TPU material FDM printing sample. The printing process parameters were studied by single factor test method, such as printing height, printing temperature, filling rate, filling direction and other effects on the tensile strength and elongation at break of the sample. The results show that the mechanical properties of TPU samples are significantly affected by 3D printing parameters. The maximum average tensile strength is 48.01±1.49 MPa and the elongation is 258±16.52%, when the printing layer is 0.2 mm, the printing temperature is 220 ℃, the filling rate is 40% and the filling direction is 0 °. Through range analysis, the influence of maximum tensile strength is as follows: filling direction ＞ filling rate ＞ printing temperature ＞ printing height.The effect on elongation at break is as follows: printing height ＞ filling Angle ＞ printing temperature ＞ filling rate.