Abstract:ZrB2-20 vol.% SiC-10 vol.% h-BN (particles) ceramic composites (ZSB) were fabricated by hot pressing under inert gas protected. ZSB samples with mean size 75 × 55 × 40 mm(3) were heated using current heating method and then cooled down to low temperature by circulating water. ZSB samples repeatedly went through thermal shock with 10-50 times under various conditions, respectively. Diverse effects on residual strength of ZSB at different experiment conditions (temperatures, thermal shock times, and heating rates) were investigated. The test results indicated that the residual strength of specimen materials all reached the maximum while the temperature was 1600 °C and thermal shock number was less than 50 times. Because ZSB samples could not stand the extremely serious hyperoxidation at very high temperature (1800 °C), the residual strength of samples decreased sharply. At 1600 °C, when the thermal shock times was 20, ZSB samples' residual strength reached the maximum, but it decreased to the lowest point while the thermal shock times was 30. So we argued that the sensitive thermal shock number was 30. Finally, we analyzed the influences on samples residual strength generated by different heating rates at the same temperature and thermal shock number; the results showed that when heating rate was equal to cooling rate, the residual strength of specimen materials reached the maximum.

Cyclic Thermal Shock Behaviors of ZrB2-SiC Laminated Ceramics Sintered with Different-Sized Particles for Each Sublayer

Cyclic Thermal Shock Behaviours of ZrB2-SiC Ultra-High Temperature Ceramics Joints Bonded with Ni Interlayer

Cyclic Ablation Behaviors of ZrB2–SiC Composites Sintered with Nano‐Sized Particles

Microstructures and Mechanical Properties of ZrB2–SiC–Ni Ceramic Composites Prepared by Spark Plasma Sintering

The Thermal Shock Resistance Of Zrb2-Sic Ultra-High Temperature Ceramics

Effect of Glass Phase on the Thermal Shock Resistance of ZrB2-SiC Ultra High Temperature Ceramic

Repeated Thermal Shock Behavior of the ZrB2–SiC–ZrC Ultrahigh-Temperature Ceramic

Sintering Temperature Effect on Microstructure, Mechanical and Electrical Properties of Multi-Layered ZrB2-based Ceramics with Thin Ti Interlayer

Mechanical and ablation properties of laminated ZrB2-SiC ceramics with Si3N4 whisker interface

Mechanical Properties and Ablation Behavior of ZrB2–SiC Ceramics Fabricated by Spark Plasma Sintering

Experiment and simulation analysis on thermal shock resistance of laminated ceramics with graphite and boron nitride interfaces

Thermal Shock Resistance of Laminated ZrB2–SiC Ceramic Evaluated by Indentation Technique

Comparative Evaluation of Two Different Methods for Thermal Shock Resistance of Laminated ZrB2-SiCw/BN Ceramics

Thermal Shock Behavior of Porous ZrB2–SiC Ceramics

Ultrahigh‐temperature tensile behaviors of ZrB2–SiC ceramics

Engineering Cf /ZrB2 -SiC-Y2 O3 for Thermal Structures of Hypersonic Vehicles with Excellent Long-Term Ultrahigh Temperature Ablation Resistance

Effects of Short Carbon Fiber on Mechanical Properties of ZrB2-SiC Ultra-high Temperature Ceramics

Effect of repeated thermal shock on mechanical properties of ZrB2-SiC-BN ceramic composites

Thermal shock behavior of SiC-whisker-reinforced diboride ultrahigh-temperature ceramics

Cyclic thermal shock behaviors of carbon fibers reinforced SiCN ceramics with architectures

The Indentation Thermal Shock Behavior of Laminated ZrB2–SiC Ceramics with Strong Interfaces