Abstract:The construction of deeply buried tunnels has intensified concerns regarding shrinkage cracking and the long-term performance deterioration of lining concrete in dry-hot environments. These issues are related to the dynamic interconversion of internal moisture states, the changing moisture behavior over time, and the evolution of calcium silicate hydrate (C-S-H) properties. However, the mechanisms underlying these phenomena are not fully understood. This study investigates the dynamics of moisture content across different states, the source and composition of evaporated water, as well as the mechanism of change in the microscopic properties of C-S-H in concrete subjected to dry-hot conditions (40°C and 60°C) and standard curing environments through tests on water loss rates, chemically bound water, and low-field nuclear magnetic resonance. The findings reveal that at 40°C and 60°C, hydration products were generated rapidly before mold removal, leading to significant increases in chemically bound water, interlayer water, and gel water, while capillary water was notably consumed. After mold removal, the rate of chemically bound water increase slowed, while interlayer water, gel water, and capillary water evaporated significantly, with gel water comprising 87.27 % and 83.51 % of the evaporated water at 40°C and 60°C, respectively. From day 1 to day 28, interlayer water, gel water, and capillary water contents decreased significantly, with reductions of up to 85.98 % at 60°C. In dry-hot environments, moisture primarily exists as chemically bound water and gel water, contrasting with standard curing conditions where capillary water is also present. The study concludes that drying of C-S-H gels leads to both positive effects, such as interlayer space compression and increased indentation modulus, and negative effects, including increased microporosity and reduced matric densification, ultimately contributing to the deterioration of long-term mechanical properties.

Shrinkage Cracking Evolvement in Concrete Cured under Low Relative Humidity and Its Relationship with Mechanical Development

Identification of Indexes That Could Reflect Early Drying Shrinkage of High Strength Concrete with Minerals

Numerical Analysis of Drying Shrinkage in Long Reinforced Concrete Structure

Shrinkage And Interior Humidity Of Concrete Under Dry-Wet Cycles

Analytical Prediction and Experimental Research on Shrinkage Cracking of Restrained Early-Age Concrete

Integrated Shrinkage, Relative Humidity, Strength Development, and Cracking Potential of Internally Cured Concrete Exposed to Different Drying Conditions

Evaluation of Shrinkage Induced Cracking in Concrete with Impact of Internal Curing and Water to Cement Ratio

Calculation of Shrinkage Stress in Concrete Structures with Impact of Internal Curing

Early Age Properties and Cracking Control of Concrete

Integrative Studies on Autogenous and Drying Shrinkages of Concrete at Early-Age

Shrinkage Stress in Concrete under Dry–wet Cycles: an Example with Concrete Column

Experimental Study on Relationship Between Shrinkage Strain and Environmental Humidity of Concrete

Experimental and Theoretical Studies on Autogenous Shrinkage of Concrete at Early Ages

Research on Cracking Mechanism of Early-Age Restrained Concrete under High-Temperature and Low-Humidity Environment

Influence of Early-age Curing Time on Shrinkage of Concrete

Micromechanical Modeling on Autogenous and Drying Shrinkages of Concrete

Restrained Shrinkage of Intermittent Casting Concrete Slab in the Early Age

Shrinkage cracking law and anti-crack inverse design in early-age concrete: A novel perspective on the development of crack resistance properties

Numerical Study of Shrinkage Cracking in Concrete and Concrete Repair Systems

Evaluation of shrinkage induced cracking in early age concrete: From ring test to circular column

Time-varying moisture characteristics and C-S-H gel properties of concrete in dry and hot environments