Abstract:Epoxy impregnated superconducting coils have better structural integrity and thermal stability. However, for REBa2Cu3O7-delta (REBCO, RE=Rare earth) coils, the mismatch of thermal expansion coefficients between epoxy and REBCO tapes is a serious problem. In this work, the temperature distribution, stress evolution during the cooling process, critical current distribution, and delamination sites inside REBCO coils impregnated using Stycast 2850FT have been studied. We measured the temperature distribution and the hoop strain in the penultimate turn of impregnated coils during the cooling process and analyzed the thermal stress evolution. No damage was observed for coils with the ratio between outer and inner diameter R-o/R-i < 1.93. The delamination behavior occurred in coils with R-o/R-i 2.37, where the coils even exhibited a two-stage delamination. The delamination mechanism of REBCO coils was proposed from three aspects: the mechanical analysis, the critical current degradation, and the microscopic analysis. In this work, we found that the actual delamination behavior may appear earlier than the steady-state temperature, and temperature distribution will push the radial stress peak toward the inner radius of the coil, making the inner turn more susceptible to delamination. Multiple delamination locations were accurately predicted and confirmed. The measured compressive hoop strain first increased from - 4212 mu epsilon to -4684 mu epsilon with the increase in R-o/R-i and then decreased to -3835 mu epsilon obviously due to delamination. This work reveals in detail the delamination mechanism in impregnated REBCO coils, which is of great significance for the development of damage-free coils. (c) 2023 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution (CC BY) license

Degradation Characteristics of a 20 T REBCO Insert Magnet After a 4.2 K Standalone Test

Design and Preliminary Tests of a 20-T REBCO Insert Coil for a 35-T All Superconducting Magnet

Design of a 20 T Class REBCO Insert in a 15 T Low Temperature Superconducting Magnet

Test of an 8.66-T REBCO Insert Coil with Overbanding Radial Build for a 1.3-Ghz LTS/HTS NMR Magnet

Numerical Analysis of Screening-Current Induced Strain in a 16 T REBCO Insert Within a 20 T Background Field

Development of YBCO Insert for a 25 T All Superconducting Magnet

Generation of 25 T with an all-superconducting magnet system: field profile and field quality measurements of a layer-wound 4 T REBCO insert coil for a 21 T LTS magnet

<i>In situ</i> detection of delamination and critical current degradation caused by the thermal stress in epoxy impregnated REBa<sub>2</sub>Cu<sub>3</sub>O<sub>7</sub>- coils

Magnetization and screening current in an 800-MHz (18.8-T) REBCO NMR insert magnet: experimental results and numerical analysis

Progress in the Construction of a 20 T REBCO Insert Coil for High-Field All-Superconducting Magnets

Electromechanical degradation of REBCO coated conductor tapes under combined tension and torsion loading

Delamination behaviors of an epoxy-impregnated REBCO pancake coil during a quench

Design and Testing of a Gas-Helium Conduction Cooled REBCO Magnet for a 300 kvar HTS Synchronous Condenser Prototype

Conceptual design of a 33 T cryogen-free magnet REBCO insert: Mechanical aspects and Protection against Thermal Runaway

Critical current degradation and delamination crack observation of epoxy-coated REBCO superconducting tapes after thermal cycles in liquid nitrogen

Influence of Excitation Sequences on Screening-Current Induced Strain in a 36 T Ultra-High-Field Magnet: Numerical Analysis and Discussion

Experiment and Numerical Modeling of Current Distributions Inside REBCO Tapes of No-Insulation Superconducting Magnet Coils Under Time-Varying Fields

Current-carrying properties of REBCO multi-filamentary tapes prepared by reel-to-reel ultraviolet picosecond laser cutting

Vortex Shaking Study of REBCO Tape with Consideration of Anisotropic Characteristics.

Experimental and Numerical Study on the Magnetization Process of Roebel Cable Segments

Exploration of the influence factors on contact resistance obtained from sudden discharge test on the large-bore metal-as-insulation REBCO magnet