Influence of interstitial carbon content on the microstructure, mechanical and electrochemical corrosion properties of CoFeNiMn multi-principal component alloys
Ouyang Zhang,Shiwu Zhang,Jianbing Hou,Kun Li,Man Zhu,Ziqi Jie,Lijuan Yao,Yongqin Liu,Zengyun Jian
DOI: https://doi.org/10.1016/j.jmrt.2023.11.006
IF: 6.267
2023-11-08
Journal of Materials Research and Technology
Abstract:In this study, the effects of carbon content on the microstructural evolution as well as compression and electrochemical corrosion properties of CoFeNiMn multi-principal component alloys (MPCAs) were investigated. A series of (Co 25 Fe 25 Ni 25 Mn 25 ) 100− x C x ( x = 4, 5, 6, 7, 8) alloys were prepared by vacuum arc melting. Increasing carbon content, the structure transits from a single face-centered-cubic (FCC) phase into a mixed structure containing FCC phase and M 23 C 6 carbides. The yield strength and hardness of the (Co 25 Fe 25 Ni 25 Mn 25 ) 100− x C x alloys were enhanced by increasing carbon content, which in turn decreases the ductility. The alloys containing eutectic carbides had a good combination of high yield strength (880 MPa), high fracture strength (2773 MPa), and large fracture strain (47%). Electrochemical measurements indicated that carbon content evidently affects the corrosion resistance of (Co 25 Fe 25 Ni 25 Mn 25 ) 100− x C x alloys in 3.5 wt% NaCl solution. Their corrosion resistance initially increases and then decreases with increasing carbon content. The increase in M 23 C 6 carbides can accelerate pitting corrosion and degenerate their corrosion resistance. These findings not only provide comprehensive understanding of the carbon-alloyed behavior in FCC-type MPCAs but also show their potential engineering application as high-performance structural materials.
materials science, multidisciplinary,metallurgy & metallurgical engineering