Ce effects on dynamic recrystallization and microstructure of the copper alloy under hot deformation behavior with different strain rate
Meng Zhou,Shunlong Tang,Yi Zhang,Xianhua Zheng,Deye Xu,Zhiyang Zhang,Yunzhang Li,Lihua Fu,Xu Li,Baohong Tian,Yanlin Jia,Yong Liu,Alex A. Volinsky,Zhiyu Han
DOI: https://doi.org/10.1016/j.jmrt.2023.04.142
IF: 6.267
2023-04-28
Journal of Materials Research and Technology
Abstract:The Cu–Ni–Sn–Ti–Cr and Cu–Ni–Sn–Ti–Cr–Ce alloys were compressed at 500–900 °C with 0.001–10 s −1 strain rates using the Gleeble 1500 deformation simulator. The effects of Ce addition on the microstructure and recrystallized grains of Cu–Ni–Sn–Ti–Cr alloy were investigated using EBSD and TEM. A constitutive equation was established to calculate the activation energy for the alloy hot deformation, and the optimal processing parameters were obtained. The corresponding texture of the Cu–Ni–Sn–Ti–Cr–Ce alloy deformed at 800 °C with 0.01 s −1 , 0.1 s −1 and 1 s −1 strain rates is the {112} Copper, {001} Cubic and {011} Goss texture. The texture of the Cu–Ni–Sn–Ti–Cr alloy deformed at 800 °C and 0.1 s −1 strain rate is the {011} Goss texture. The strain rate and Ce addition can change the alloy texture. The precipitation phase in Cu–Ni–Sn–Ti–Cr (-Ce) alloy is mainly CuNi 2 Ti phase, and the addition of Ce can promote the precipitation of fine nanoscale precipitation phase in the alloy. Moreover, the addition of Ce can promote the dynamic recrystallization of the alloy, but the dynamic recrystallization of the alloy is suppressed with the increase of the hot deformation rate at the heat deformation temperature of 800 °C.
materials science, multidisciplinary,metallurgy & metallurgical engineering