Effect of Ce on Microstructure and Deformation Performance of Mg-2Zn-Mn Alloy

PENG Jian,FAN Shi-bo,SHE Huan,PAN Fu-sheng

DOI: https://doi.org/10.3969/j.issn.1001-4381.2010.08.015

2010-01-01

Abstract:The effects of different Ce contents on the microstructure, mechanical properties and performance of hot deformation were investigated. By methods of OM, X-ray, SEM, XRD, tensile test at room temperature and hot compression test on Gleeble 1500D thermal-mechanical simulator, the changes of Mg-2Zn-Mn-xCe alloys in microstructure, second phase and mechanical performance were compared. The results show that with the increasing of Ce content, the as cast microstructure becomes coarse and then fine, while the strength and plasticity decrease firstly and then increase to the value of 200MPa for UTS (ultimate tensile strength), 74MPa for YS (yield strength) and 20% for elongation, and the deformation resistance of hot compression increases at the same time. When traces Ce adding, the compound particle becomes fine, the number of MgZn phase reduces, the Ce2Zn17 phase appears, some compound particles lie in secondary dendrite arm space. When Ce content is more than 0.37%, the particles change into Ce3Zn, 2 and CeZn3 phases, and with the increasing of the Ce content, the particles mainly exist in the primary dendrites spacing in shape of network.