Abstract:Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured macrostructure consisting of elongated polycrystalline MgB2 fibers separated by elongated pores. The superconducting Tc, Jc and Fp were correlated with the macrostructure and grain size. Grain size increased with HT time at both 600C and 700C. Jc and hence Fp decreased monotonically but not linearly with grain size. Overall, it was observed that at 700C, the MgB2 reaction was more or less complete after as little as 30 min; at 600C, full reaction completion did not occur until 71 h. into the HT. Transport, Jct(B) was measured in a perpendicular applied field, and the magnetic critical current densities, Jcm\bot(B) and Jcm{\phi}(B), were measured in perpendicular and parallel (axial) applied fields, respectively. Particularly noticeable was the premature dropoff of Jcm\bot(B) at fields well below the irreversibility field of Jct(B). This effect is attributed to the fibrous macrostructure and its accompanying anisotropic connectivity. Magnetic measurements with the field directed along the strand axis yielded a critical density, Jcm\bot(B), for current flowing transversely to the strand axis that was less than and dropped off more rapidly than Jct(B). In the conventional magnetic measurement, the loop currents that support the magnetization are restricted by the lower of Jct(B) and Jcm{\phi} (B). In the present case the latter, leading to the premature dropoff of the measured Jcm(B) compared to Jct(B) with increasing field. This result is supported by Kramer plots of the Jcm{\phi} (B) and Jct(B) data which lead to an irreversibility field for transverse current that is very much less than the usual transport-measured longitudinal one, Birr,t.

Heat Transfer Analysis of MgB2 Coil in Heat Treatment Process for Future Fusion Reactor

Conceptual Design of a HTS CICC Coil for Fusion Devices based on Bi-2223 Tapes

The Conceptual Optimal Design of a 300MJ High Temperature Superconducting Magnet

Mechanical analysis of an MgB2 1.5 T MRI main magnet protected using Coupling Loss Induced Quench

Influence of the Preparation Process on Microstructure, Critical Current Density and Tc of MgB2 Powder-In-Tube Wires

Thermomechanical Behavior of the HL-LHC 11 Tesla Nb3Sn Magnet Coil Constituents during Reaction Heat Treatment

Fabrication of MgB2 Coil with the Center Field of 5.71 Tesla Using 520‐m Inner Magnesium Diffusion Wire

High temperature heat treatment of B precursor and P.I.T. process optimization to increase Jc performances of MgB2-based conductor

The magnetic cage

Fabrication and Properties of Multifilamentary MgB2 Wires by In-Situ Powder-in-tube Process

Coating Thick MgB 2 Layer on Stainless Steel Substrate

Transport and magnetic Jc of MgB2 strands and small helical coils

Drawing induced texture and the evolution of superconductive properties with heat treatment time in powder-in-tube in-situ processed MgB2 strands

Bulk superconducting materials as a tool for control, confinement, and accumulation of polarized substances: the case of MgB2

Effect of Heat Treatments under High Isostatic Pressure on the Transport Critical Current Density at 4.2 K and 20 K in Doped and Undoped MgB2 Wires

Improved cryogenic stability by thermal insulation between forced-flow gas-cooled REBCO conductors in fusion magnets

The Preparation of MgB 2 Conductors for Magnet Application of SMES in WST

Influence of heat treatment excursion on critical current and residual resistivity ratio of ITER Nb3Sn strands

Improving superconducting properties of 100 m class MgB 2 wire with 18+1 filaments produced via internal Mg diffusion process

Electromagnetic, stress and thermal analysis of the Superconducting Magnet

Influences of Heat Treatment and Doping on Microstructure and Superconducting Properties of MgB2 Superconductor