Structural Degradation and Elemental Variations in an Ex-Service First-Stage Gas Turbine Blade

Hui Lu,Wenhan Zhang,Yanhui Chen,Yadi Zhai,Wenshuai Wang,Haibo Long,Ang Li,Xiaodong Han

DOI: https://doi.org/10.1016/j.matchar.2022.112596

IF: 4.537

2023-01-01

Materials Characterization

Abstract:First-stage gas turbine blades in an airplane undergo extreme operating conditions under high temperature and high stress conditions, usually causing nonhomogeneous microstructural degradation. The detailed characterization of temperature- and stress-induced microstructural degradation, dislocation and elemental variation are keys for failure analysis. In our study, we systematically investigate microstructural degradation on an ex-serviced second-generation superalloy-based turbine blade from an aeroengine. Defects in trailing edges are mainly sparse dislocation networks, exhibit a low stacking fault density, and are in an initial rafting stage in most regions. The most severely degraded region is in a middle stage of creep, with high densities of network dislocations in the γ phase and stacking faults in the γ’ phase. An overall reorganization of ex-service turbine blades is built, and the relationship between service and microstructural degradation is revealed. With this study, we provide guidance on microstructural degradation evaluation and failure analysis in conventional single-crystal turbine blades.