Abstract:Single-crystal superalloy is the key material of turbine blade and hot end parts in aerospace field. The second generation nickel-based single crystal superalloy has been widely used because of its low cost and excellent high temperature properties. At present, the research on microstructure of superalloys at high temperature mainly depends on SEM and TEM observation after heating and loading experiment. However, such kind of work lacks real-time characterization capabilities. Carrying out in situ experiments has an important significance for understanding the real time deformation behavior and microstructure evolution of superalloys. Therefore, the development of an in situ high temperature (above 1000 degrees C) mechanical testing equipment for SEM faces huge challenges. In this work, high temperature tensile experiment at 1150 degrees C of a second generation single crystal nickel-based superalloy were carried out by means of a self-developed in situ heating tensile platform which can used in SEM. A high quality experimental data and serial SEM images were obtained in the course of tensile testing at 1150 degrees C. The analysis of force-displacement curve shows that the yield strength and fracture strength of the specimen are 580 and 620 MPa, respectively. The sequential SEM images during this research confirm that there is no obvious shape and size change for gamma and gamma' during the elastic deformation, and microstructure changing during plastic stage is mainly due to gamma phase widening which is parallel to the stress axis. The results show that the original micro-voids of samples are the weakness in high temperature tensile test at 1150 degrees C, the fracture direction is almost perpendicular to the stress axis, the crack propagated by passing the gamma' phase and through in the gamma phase, and ultimately, temperature and stress induced adjacent holes connection leading to the sample fracture.

The Unique Influence of 1000°C High-Speed Rotation Simulated Turbine Blade Working Conditions on Microstructural Degradation of Single-Crystal Superalloy Nialreru

Microstructure Degradation of Service-Exposed Turbine Blades Made of Directionally Solidified DZ125 Superalloy

Dependence of Microstructural Evolution on the Geometric Structure for Serviced DZ125 Turbine Blades

Investigation on low cycle fatigue of nickel‐based single crystal turbine blade in different regions

Investigation on low cycle fatigue of nickel-based single crystal turbine blade in different regions: Untersuchung der Kurzzeitermüdung von nickelbasierten Monokristall-Turbinenschaufeln an verschiedenen Stellen

Vibration Fatigue Behavior and Failure Mechanism of Ni-based Single-Crystal Film Cooling Hole Structure under High Temperature

Failure mechanism of single-crystal superalloy NiAlReRu components with film cooling holes under the coupling high-speed rotating and high temperature condition

Low Cycle Fatigue Behavior and Crack Initiation Mechanism of Ni-based Single Crystal Curved Thin-Walled Blade Simulator Specimen with Film Cooling Holes

Research on Low Cycle Fatigue Damage and Macroscopic Anisotropic Constitutive Model of Ni-based Single Crystal Superalloy at Different Temperatures

A Study of the Internal Deformation Fields and the Related Microstructure Evolution during Thermal Fatigue Tests of a Single-Crystal Ni-Base Superalloy

Experimental Investigation and Modelling of Microstructure Degradation in a DS Ni-based Superalloy Using a Quantitative Cross-Correlation Analysis Method

Creep Behavior and Deformation Mechanism of a Third-Generation Single Crystal Ni-Based Superalloy at 980 °C

Effect of Overheating Treatment on Microstructure and Stress Rupture Properties of a Nickel-Based Single-Crystal Superalloy

Degradation and Dislocation Evolution of the Nickel-Based Single Crystal Superalloy DD6 under the Coupling High-Speed Rotating and High Temperature Environments

Microstructural Stability of Single Crystal Superalloy DD402 and Its 1st Stage Turbine Blades

Deformation mechanisms of low cycle fatigue of a fourth generation Ni-based single crystal superalloy

Competitive Cracking Behavior and Microscopic Mechanism of Ni-based Superalloy Blade Respecting Accelerated CCF Failure

Simulation and Experimental Investigation of Grain Structure, Residual Stress,γ′ Phases in Single Crystal Blade

Microstructural Rejuvenation in a Ni-based Single Crystal Superalloy

Life Study of Nickel-Based Single Crystal Turbine Blades: Viscoplastic Crystallographic Constitutive Behavior

Investigation of In Situ 1150 ℃ High Temperature Deformation Behavior and Fracture Mechanism of a Second Generation Single Crystal Superalloy