Abstract:The complex failure behavior of turbine blades under cyclic creep is of great significance to the safety of aeroengines . In this study, the deformation regulation and fracture mechanism of a single-crystal Ni-based superalloy DD6 under cyclic loading at 980 °C are investigated, and the strengthened rupture life and fracture deformation are clearly exhibited. Scanning electron microscopy and electron backscatter diffraction observations were conducted to reveal the deformation and fracture mechanisms. A smaller particle spacing of the γ/γ' interface was observed under cyclic loading/unloading, which restricted dislocation movement and reduced the creep rate. This led to an extended creep life of steady creep stage, and the delay of the accelerated creep stage. Additionally, the creep deformation distribution and slip system activation affected the fracture toughness under the accelerated creep stage, leading to an increase in the creep fracture strain under cyclic loading/unloading. Finally, the fracture mechanism affected by cyclic loading is discussed based on inner and surface cracks. Cyclic loading/unloading promotes the multisource initiation of surface cracks, which improves loading capacity. Furthermore, cyclic loading/unloading promotes the generation of secondary cracks deflected from crack tips. The high residual compressive stress at the crack tip delays creep-crack initiation during unloading, leading to a decrease in the creep-crack propagation rate. These factors led to cyclic strengthening at different scales.

Creep/fatigue accelerated failure of Ni-based superalloy turbine blade: Microscopic characteristics and void migration mechanism

Competitive Cracking Behavior and Microscopic Mechanism of Ni-based Superalloy Blade Respecting Accelerated CCF Failure

Microstructure Degradation of Service-Exposed Turbine Blades Made of Directionally Solidified DZ125 Superalloy

Service Damage Mechanism and Interface Cracking Behavior of Ni-based Superalloy Turbine Blades with Aluminized Coating

Thermomechanical Fatigue Experiment and Failure Analysis on a Nickel-Based Superalloy Turbine Blade

Creep Behavior and Deformation Mechanism of a Third-Generation Single Crystal Ni-Based Superalloy at 980 °C

Microstructure and mechanical degradation of K403 Ni-based superalloy from ultra-long-term serviced turbine blade

Accelerated damage mechanisms of aluminized superalloy turbine blades regarding combined high-and-low cycle fatigue

Thermomechanical fatigue behavior and failure mechanism of a nickel-based directional solidification column crystal superalloy

Unveiling the failure mechanism on creep response of a casting Ni-based superalloy in thin-wall thickness

Failure mechanism of single-crystal superalloy NiAlReRu components with film cooling holes under the coupling high-speed rotating and high temperature condition

Experimental Study and Creep-Fatigue Life Prediction of Turbine Blade Material DZ125 Considering the Nonholding Effect and Coupling Effect of Stress and High Temperature

Deformation mechanisms of low cycle fatigue of a fourth generation Ni-based single crystal superalloy

Microstructure degradation and residual low cycle fatigue life of a serviced turbine blade

The Unique Influence of 1000°C High-Speed Rotation Simulated Turbine Blade Working Conditions on Microstructural Degradation of Single-Crystal Superalloy Nialreru

Direct Investigation on High Temperature Tensile and Creep Behavior at Different Regions of Directional Solidified Cast Turbine Blades

Creep feed grinding induced gradient microstructures in the superficial layer of turbine blade root of single crystal nickel-based superalloy

Experimental investigation on creep strengthening phenomenon of a Ni-based single crystal superalloy under cyclic loading and unloading conditions

Numerical Simulation of Creep Damage and Life Prediction of Superalloy Turbine Blade

Tensile, Creep Behavior and Microstructure Evolution of an As-Cast Ni-based K417G Polycrystalline Superalloy

Thermo-mechanical Fatigue Deformation and Fracture Mechanisms of Nickel-Based Powder Metallurgy Superalloy