Nanoscale engineering of low-misfit TiB 2 /Al 3 (Sc,Zr)/α-Al multi-interface to improve strength-ductility synergy for direct energy deposited aluminum alloy
Yang Li,Yihao Wang,Lei Hu,Tingting Chen,Gang Ji,Han Chen,Hongze Wang,Haowei Wang,Zhe Chen
DOI: https://doi.org/10.1016/j.addma.2023.103913
IF: 11
2023-12-08
Additive Manufacturing
Abstract:The nature of the interface between ceramic particle (CP) and metal matrix is critical to obtain solidification microstructures with optimal mechanical properties of CP-reinforced Al alloys in additive manufacturing. Generally, when the lattice misfit between the CP (e.g., TiB 2 ) and the α-Al matrix is higher than 4%, the interfacial coherency reduces, lowering the effectiveness of CPs. Here, we demonstrate that an L1 2 three-dimensional compound (3DC), which possesses lattice misfit with α-Al lower than 1%, can be introduced in between TiB 2 and α-Al via properly regulating the solidification cooling rate. In the 5TiB 2 /Al-4.5Mg-0.7Sc-0.2Zr (wt.%) as a model system, the lattice coherence of the TiB 2 /α-Al interface is tailored by introducing a 10-30 nm thick Al 3 (Sc,Zr) 3DC interphase when the cooling rate is increased to ~1000 o C/s. But, further increasing the cooling rate to ~6800 o C/s, only Al 3 (Sc,Zr) two-dimensional compound (2DC) with an apparent lattice strain forms at the interface. Taking advantage of the cooling rate (10 2 -10 3 o C/s) provided by laser direct energy deposition (L-DED), the low-misfit "TiB 2 /Al 3 (Sc,Zr) 3DC/α-Al" multi-structural interfaces are acquired, enabling the 3.56TiB 2 /Al-4.36Mg-0.72Sc-0.22Zr alloy as fabricated with L-DED to achieved improved strength-ductility synergy (yield strength 257 MPa, elongation 13.8%) due to the isotropically fine Al grain structure and the homogenous TiB 2 particle dispersion. The outcome of this study provides fundamental knowledge on designing "ceramic/coherent primary interphase/metal matrix" multi-structural interfaces to improve the mechanical properties of engineering metallic materials manufactured by rapid solidification techniques, such as DED additive manufacturing (AM).
engineering, manufacturing,materials science, multidisciplinary