Abstract:Carbon fiber reinforced carbon aerogel composites were prepared by impregnating the fiber preform,gel aging,supercritical drying and carbonization.Resorcinol (R)-furfural (F)alcohol sol was synthesized by isopro-panol (I)as solvent,hexamethylenetetramine (H)as catalyst.The effects of sol proportion on densities,micro-structures and mechanical properties of carbon fiber reinforced carbon aerogel insulation composites were investiga-ted.The results show that the densities of carbon fiber reinforced carbon aerogel insulation composites decrease gradually,the pores diameter and the amount of large pores in matrix carbon aerogels and the interface formed with carbon fiber increase,the strength of carbon fiber reinforced carbon aerogel insulation composites decreases with the increases of amount of substance ratio for isopropanol and resorcinol.When isopropanol and resorcinol amount of substance ratio increases from 18 to 28,the compressive strength decreases from 2.498 MPa (strain 10%)to 0.716 MPa (strain 10%),tensile strenghth decreases from 2.019 MPa to 1.001 MPa,bending strength decreases from 3.984 MPa to 1.818 MPa.The densities of carbon fiber reinforced carbon aerogel insulation composites increa-ses firstly and then decreases,the pores diameter and the the amount of large pores in matrix carbon aerogels and in-terface formed with carbon fiber decreases firstly and then increases,the strength of carbon fiber reinforced carbon aerogel insulation composites increases fistly and then decreases with the increase of amount of substance ratio for hexamethylenetetramine and resorcinol.The densities and the strength of carbon fiber reinforced carbon aerogel in-sulation composites are biggest when amount of substance ratio for hexamethylenetetramine and resorcinol is 0.008 5,the compressive strength is 1.066 MPa (strain 10%),the tensile strenghth is 1.256 MPa,bending strength is 3.5 5 6 MPa.

Mechanical and Thermal Insulation Properties of Carbon Fibre-Reinforced Carbon Aerogel Composites

Carbon Aerogel Composites Prepared by Ambient Drying and Using Oxidized Polyacrylonitrile Fibers As Reinforcements

Effects of Carbonization Temperature on Mechanical and Thermal Insulation Properties of Carbon Aerogel Composites Using Phenolic Fibers As Reinforcement

Effects of Carbon Nanotubes and Carbon Fiber Reinforcements on Thermal Conductivity and Ablation Properties of Carbon/phenolic Composites

Preparation and Properties of PAN-based Carbon Fiber-Reinforced SiCO Aerogel Composites

The Microstructure and Ablation Behavior of Carbon Fiber/phenolic Aerogel Composites

Carbon fiber reinforced carbon aerogel composites for thermal insulation prepared by soft reinforcement

Tailoring microstructures of carbon fiber reinforced carbon aerogel-like matrix composites by carbonization to modulate their mechanical properties and thermal conductivities

Anti-oxidation Performance of Carbon Aerogel Composites with SiCO Ceramic Inner Coating

Preparation of a Carbon Fibre-Reinforced Carbon Aerogel and Its Application As a High-Temperature Thermal Insulator.

Effects of sol proportion on mechanical properties of carbon fiber reinforced carbon aerogel insulation composites

Fabrication and Properties of Carbon/carbon-Carbon Foam Composites

Insight into the origin of oxidation behaviors of carbon fiber reinforced carbon aerogel composites with different porous skeletons

Preparation and Mechanical Properties of Carbon/carbon Composites with High Textured Pyrolytic Carbon Matrix

Fabrication of Large Aerogel-Like Carbon/Carbon Composites with Excellent Load-Bearing Capacity and Thermal-Insulating Performance at 1800 °C

Mechanically Strong and Thermally Responsive Cellulose Nanofibers/Poly(N-isopropylacrylamide) Composite Aerogels

Performance of the RF Aerogels Composited with PAN Pre-Oxidized Fibers

Thermophysical Properties of Carbon/carbon Composites and Physical Mechanism of Thermal Expansion and Thermal Conductivity

Carbon Foam-Reinforced Polyimide-Based Carbon Aerogel Composites Prepared via Co-Carbonization as Insulation Material

Organic Aerogel-Impregnated Low-Density Carbon/Carbon Composites: Preparation, Properties and Response under Simulated Atmospheric Re-Entry Conditions