Abstract:A low-density, high-specific surface area, high-strength and large-sized carbon aerogel preparation process is a key technology in the industrial application of aerogel science. In recent years, ingenious nanostructure design, along with salt templates, drying optimization and other strategies have been applied by numerous scientists. As a result, the specific surface area of carbon aerogel has significantly increased and the density reduced. However, the preparation of high-strength and large-sized intact carbon aerogel at low cost is still a challenge due to the limitations of thermal treatment equipment and drying process. In this study, we propose an improved preparation method of ambient pressure solvothermal polymerization and auxiliary ambient pressure drying by the principle of acid–base two-step catalysis using resorcinol and furfural as raw materials. Resultantly, the condensation and cross-linking reaction process is stabilized by the ambient pressure solvothermal polymerization, which effectively reinforces the interfacial bonding between primary particles and forms a high-strength skeleton. The breaking strength of the aerogels reach up to 9.74 MPa. The auxiliary ambient pressure drying can greatly reduce the drying shrinkage and density of the aerogel and solve the problems of drying deformation and cracking of large-sized carbon aerogel. The drying shrinkage and density of the obtained carbon aerogels are reduced to 3.22% and 0.203 g/cm 3 , respectively, and the specific surface area reaches 675.057 m 2 /g. Moreover, the large-sized sample (70 mm (d) × 25 mm (h)) can also be prepared by this method since the strength of skeleton can resist the capillary force of pore structure, and the nanoporous architecture can be perfectly retained. Therefore, this study provides a new preparation scheme for the industrial large-scale production and application of carbon aerogel.

Preparation of a Carbon Fibre-Reinforced Carbon Aerogel and Its Application As a High-Temperature Thermal Insulator.

Carbon fiber reinforced carbon aerogel composites for thermal insulation prepared by soft reinforcement

Facile preparation of lightweight and robust carbon aerogel monoliths for high-temperature thermal insulation and oil-water separation

Cellulose Nanofibril (CNF) Based Aerogels Prepared by a Facile Process and the Investigation of Thermal Insulation Performance

Carbon-Fiber Felt Reinforced Carbon/Alumina Aerogel Composite Fabricated with High Strength and Low Thermal Conductivity

ZrC/C aerogel with high compressive strength by a carbothermic process

Preparation of micro-convex rough interface carbon aerogels with cellulose-lithium bromide (LiBr) molten salt hydrate gelled system and application of oil-water separation

Synthesis of carbon aerogels with controlled morphology and pore structure to modulate their bulk density and thermal conductivity via a quick one-pot preparation strategy

Silica-Bacterial Cellulose Composite Aerogel Fibers with Excellent Mechanical Properties from Sodium Silicate Precursor

Fabrication of Large Aerogel-Like Carbon/Carbon Composites with Excellent Load-Bearing Capacity and Thermal-Insulating Performance at 1800 °C

Recycling Coal Fly Ash for Super-Thermal-Insulating Aerogel Fiber Preparation with Simultaneous Al2O3 Extraction

Low-density, high-strength and large-scaled monolithic carbon aerogels fabricated via modified ambient pressure drying

Facile preparation of ZrCO composite aerogel with high specific surface area and low thermal conductivity

Recycling Coal Fly Ash for Super-Thermal-Insulating Aerogel Fiber Preparation with Simultaneous Al 2 O 3 Extraction.

Superelastic Cobalt Silicate@Resorcinol Formaldehyde Resin Core-Shell Nanobelt Aerogel Monoliths with Outstanding Fire Retardant and Thermal Insulating Capability

Fabrication of the SiC/HfC Composite Aerogel with Ultra-Low Thermal Conductivity and Excellent Compressive Strength

Recycling Coal Fly Ash for Super-Thermal-Insulating Aerogel Fiber Preparation with Simultaneous Al<sub>2</sub>O<sub>3</sub> Extraction

Carbon Aerogel with High Thermal Conductivity Enabled by Shrinkage Control

Monolithic carbon aerogels within foam framework for high-temperature thermal insulation and organics absorption

Carbon Aerogel for Insulation Applications: A Review

Robust Silica-Bacterial Cellulose Composite Aerogel Fibers for Thermal Insulation Textile