Abstract:Carbon aerogels, owing to the high-temperature durability and low thermal conductivity, are promising candidates for high-temperature thermal insulation used in inert atmospheres. However, significant drying shrinkage poses challenges in fabricating large-sized carbon aerogels and optimizing their thermal insulation properties. Herein, we report the synthesis of monolithic carbon aerogels with low drying shrinkage and controllable nanostructures by adding self-crosslinked chitosan to provide reaction sites and three-dimensional network support based on the traditional resorcinol–formaldehyde method in an acetic acid environment. Owing to the increased cross-linking degree of resorcinol–formaldehyde gel from the polymerization and hydrogen bonding between chitosan and resorcinol–formaldehyde oligomers, the skeleton of gel network is strengthened and the shrinkage during supercritical drying is as low as 1.51 %, resulting in a good monolithic shape of carbon aerogel (130 × 130 × 15 mm). Besides, they exhibit typical nanoporous characteristics with uniform and small particle size (9–130 nm) and low density (0.070–0.221 g·cm−3), achieving a low thermal conductivity of 0.047 W·m−1·K−1 at 1100 °C and high compressive strength of 1.80 MPa (density of 0.138 g·cm−3). This method facilitates the production of carbon aerogels with low shrinkage, minimal defects, low density, and small pore size, rendering them suitable for applications requiring large dimensions and low defect levels, such as fiber-reinforced composites and high-performance thermal insulators.

Carbon fiber reinforced carbon aerogel composites for thermal insulation prepared by soft reinforcement

Carbon Aerogel Composites Prepared by Ambient Drying and Using Oxidized Polyacrylonitrile Fibers As Reinforcements

Preparation of a Carbon Fibre-Reinforced Carbon Aerogel and Its Application As a High-Temperature Thermal Insulator.

Performance of the RF Aerogels Composited with PAN Pre-Oxidized Fibers

Ultralight carbon fiber felt reinforced monolithic carbon aerogel composites with excellent thermal insulation performance

Ionothermal Synthesis of Fiber-Reinforced Carbon Aerogel Composites from Fructose with High Mechanical and Thermal Insulation Properties

Carbon Aerogel for Insulation Applications: A Review

Preparation of Flexible Fiber-Reinforced Aerogel Composites for Thermal Insulation

Synthesis of Environmentally Friendly Nanoporous Monolithic Carbon Aerogels Via Ambient Pressure Drying for High-Temperature Thermal Insulators

Mechanical and Thermal Insulation Properties of Carbon Fibre-Reinforced Carbon Aerogel Composites

Carbon-Fiber Felt Reinforced Carbon/Alumina Aerogel Composite Fabricated with High Strength and Low Thermal Conductivity

Carbon Foam-Reinforced Polyimide-Based Carbon Aerogel Composites Prepared via Co-Carbonization as Insulation Material

Carbon Aerogel with High Thermal Conductivity Enabled by Shrinkage Control

Ultralow Thermal Conductivity of Single-Atom Doped Carbon Aerogel Synthesized with a Facile Ambient-Pressure-Drying Strategy

Shrinkage and pore structure in preparation of carbon aerogels

Preparation and Properties of PAN-based Carbon Fiber-Reinforced SiCO Aerogel Composites

Synthesis of Structure Controllable Carbon Aerogel with Low Drying Shrinkage and Scalable Size As High-Temperature Thermal Insulator

Preparation of carbon/silica composite aerogel and application of fire insulation

Preparation and Properties of Fiber Reinforced SiO_2 Aerogel Insulation Composites

Cellulose Nanofibril (CNF) Based Aerogels Prepared by a Facile Process and the Investigation of Thermal Insulation Performance

Mechanically Strong and Thermally Responsive Cellulose Nanofibers/Poly(N-isopropylacrylamide) Composite Aerogels