Abstract:Nano-materials are increasingly being used as modified binder for improve the performance of cementitious materials. In this paper, nano-SiO2 and nano-Al2O3 were incorporated into the geopolymers formed by the mixture of construction solid waste (recycled concrete fine powder) and industrial solid waste (slag). The effects of the type and content of nanomaterials on the early reaction kinetics, physical and mechanical properties and microstructure of geopolymer composites were explored. Results show that the addition of nanomaterials mainly affected the dissolution stage of geopolymerization, played a nucleation effect and improved the reaction rate. The promotion effect of nano-Al2O3 was slightly greater than that of nano-SiO2. Based on the results of JMAK model, the formation of geopolymers composites was an one-dimensional heterogeneous nucleation control reaction, which followed a plate-like structure thickening mechanism. The addition of nanomaterials shortened the setting time. The incorporation of nano-Al2O3 was beneficial to improve the fluidity of geopolymer. Furthermore, the addition of the two nanomaterials could improve the compressive strength of geopolymers. The compressive strength tended to first increase and then decrease with increasing nano-SiO2 or nano-Al2O3 content. The optimal mixing ratio of nano-silica and nano-alumina were 1.2% and 1.6% respectively, and the 28-day compressive strengths were both 59.05 MPa, which were 23.35% higher than that without nano-materials. XRD and SEM-EDS analysis indicate that the incorporation of nanomaterials had no impact on the type of final products, but increased their number, particularly calcium-based gel products. The internal structure of geopolymer with nanomaterials was more dense and uniform than that without nanomaterials. The MIP observed that the addition of the two nano-materials reduced the porosity in the matrix, the number of macropores and the pore fractal dimension. The pore fractal dimension of geopolymer was negatively correlated with the compressive strength.

Self-compensating Geopolymer Utilizing Nano-Clay and Chopped Basalt Fibers

Experimental Study on the Flexural Fatigue Performance of Slag/fly Ash Geopolymer Concrete Reinforced with Modified Basalt and PVA Hybrid Fibers

Performance Characteristics of Micro Fiber-Reinforced Ambient Cured One-Part Geopolymer Mortar for Repairing

Preparation and curing method of red mud-calcium carbide slag synergistically activated fly ash-ground granulated blast furnace slag based eco-friendly geopolymer

Study on the Geopolymer Based on Fly Ash and Slag

Shrinkage and Mechanical Properties of Fibre-Reinforced Blast Furnace Slag-Steel Slag-Based Geopolymer

An efficient approach for sustainable fly ash geopolymer by coupled activation of wet-milling mechanical force and calcium hydroxide

Mechanism, characterization and factors of reaction between basalt and alkali: Exploratory investigation for potential application in geopolymer concrete

Effects of Spodumene Flotation Tailings on Mechanical Properties of Acid-Based Geopolymer Mortar

Interfacial Behavior of Slag, Fly Ash, and Red Mud-Based Geopolymer Mortar with Concrete Substrate: Mechanical Properties and Microstructure

Influence of the Activator Concentration and Solid/Liquid Ratio on the Strength and Shrinkage Characteristics of Alkali-Activated Slag Geopolymer Pastes

Mechanical behavior and microstructure evolution of slag-fly ash based geopolymer stabilized sand

Study on the Reinforced Properties of Geopolymer Fibers with a Sustainable Development Role

Strength and Microstructure Characteristics of Blended Fly Ash and Ground Granulated Blast Furnace Slag Geopolymer Mortars with Na and K Silicate Solution

The Effects of the Sequential Addition of Synthesis Parameters on the Performance of Alkali Activated Fly Ash Mortar

Fresh and Hardened Properties of One-Part Fly Ash-Based Geopolymer Binders Cured at Room Temperature: Effect of Slag and Alkali Activators

Synthesis and Performance Evaluation of Nano-Calcium Carbonate-Modified Geopolymers Incorporating Fly Ash and Manganese Slag: A Comprehensive Investigative Study

Modeling and optimization of fly ash–slag-based geopolymer using response surface method and its application in soft soil stabilization

Reaction kinetics, mechanical properties, and microstructure of nano-modified recycled concrete fine powder/slag based geopolymers

Silty Clay Stabilization Using Metakaolin-Based Geopolymer Binder

Optimizing Toughness and Cost-Effectiveness in One-Part Geopolymers Via Fiber Reinforcement: A Comprehensive Investigation of PVA, PE, and Glass Fibers