Influence mechanism of pin thread in friction stir welding of magnesium alloys based on the relationship between microstructure and mechanical properties
Liangwen Xie,Xiong Xiao,Xianyong Zhu,Yuexiang Fan,Cheng Jiang,Yulai Song
DOI: https://doi.org/10.1016/j.jmatprotec.2023.117870
IF: 6.3
2023-03-01
Journal of Materials Processing Technology
Abstract:The texture generated in friction-stir welding (FSW) of magnesium alloys leads to anisotropy in mechanical properties. For this purpose, three thread depths (0 mm, 0.4 mm, 0.75 mm) of tool pins were designed to study the influence mechanism of the pin thread on the microstructure and mechanical properties of welded joints. The results showed that with increasing thread depth, the material flow was more adequate, and the welding process generated more low-angle grain boundaries, which promoted continuous dynamic recrystallization and grain refinement. However, the intensity and amplitude of the texture within the stir zone (SZ) also increased. As the thread depth increased from 0 mm to 0.75 mm, the texture intensity in the center of the SZ increased from 29.1 times to 61.7 times the random distribution. The variation of texture intensity and orientation along the transverse direction introduced anisotropy, which dominated the non-uniform distribution of microhardness and yield strength within the SZ, and the appearance of distinct soft zones at the edges of the SZ. Thus, the welded joints obtained with 0.75 mm thread depth had relatively poor mechanical properties. In contrast, the welded joints obtained with 0.4 mm thread depth had better mechanical properties with a tensile strength of 256.6 MPa, elongation of 14 %, and joint efficiency of 94.3 %. Therefore, controlling the texture should be the focus of attention. This study proposes that weakening texture outside of adequate flow is an important prerequisite for the tool design of the FSW of magnesium alloys.
materials science, multidisciplinary,engineering, manufacturing, industrial