Microstructure, Toughness, and Tribological Properties of Laser Cladded Mo2FeB2-based Composite Coating with in Situ Synthesized WC and La2O3 Addition

Hao Zhang,Yingjun Pan,Yang Zhang,Guofu Lian,Qiang Cao,Linzhi Que

DOI: https://doi.org/10.1016/j.surfcoat.2022.128947

IF: 4.865

2022-01-01

Surface and Coatings Technology

Abstract:Mo2FeB2-WC-La2O3 composite coatings were prepared using a preplaced method of laser cladding. The forming quality, microstructure, distribution of La, microhardness, fracture morphology, fracture toughness, and tribo-logical properties were examined. The effect of La2O3 on the microstructure and properties of the coatings was analyzed. The results showed that the metallurgical bonding between the coating and substrate was significantly improved. La2O3 had no significant effect on the phases of the composite coatings. The microstructure growth of the La2O3 coating had no obvious direction and a block-like structure. The microstructure was initially refined and then coarsened with an increase in La2O3; La was found to exist at the Mo2FeB2 phase grain boundaries. The microhardness of the Mo2FeB2-WC coating was 1584.6 HV0.5. The microhardness of the composite coating that contained 0.3 wt% La2O3 reached 1494.7 HV0.5; its coefficient of friction (COF), wear rate, and fracture toughness were 0.31, 3.13 x 10(-5) mm(3)/Nm, and 14.35 MPa.mm(1/2), respectively. The crack resistance of the composite coating was the highest at 0.3 wt% La2O3 addition. The wear mechanisms of the coatings containing La2O3 were typical abrasive wear, and the coating without La2O3 was a combined mechanism of slight adhesive and abrasive wear. The coating exhibited an evident brittle fracture morphology.