Abstract:Low interfacial adhesion seriously limits the wide application of PBO fiber in composites. To solve this problem, a novel hierarchical reinforcement strategy was developed by introducing epoxy sizing, nanoreinforcement of amino-functionalized silicon dioxide (SiO2–NH2), and an interfacial compatibilizer of 2,6-bis(2-hydroxy-4-aminophenyl) benzobisoxazole (HABO) onto poly(p-phenylene benzobisoxazole) (PBO) fibers via a facile dip-coating approach. SiO2–NH2 and HABO were uniformly dispersed in epoxy sizing, forming an active interface layer. On this basis, wettability, surface roughness of the PBO fiber, and compatibility with the resin matrix were significantly improved, which gave 88.4 and 40.4% enhancement in the interfacial shear strength and interlaminar shear strength of the corresponding composites, respectively. Moreover, it should be noted that the outstanding mechanical and thermal properties of the PBO fiber were not impaired during the sizing treatment. In summary, our work provides an effective and damage-free approach to improve the interfacial adhesion of PBO/epoxy composites.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c14975?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c14975</a>.ATR-FTIR spectra and TG curves of SiO2–OH and SiO2–NH2; ATR-FTIR spectrum of HABO; TG curves of various PBO fibers; SEM image of PBO-SH0; EDS elemental mappings and cross-sectional SEM images of PBO-SN0, PBO-SN0.5, PBO-SN2, and PBO-SN1-H0.1; three-dimensional (3D) renderings of H-256 and HABO; debonded morphology of PBO-SN0; elemental compositions of SiO2–OH and SiO2–NH2; and percentage contents of different functional groups on pristine PBO and PBO-SN0 (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c14975/suppl_file/am0c14975_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Environmentally Friendly Sizing Strategy for PBO Fiber-reinforced Composites Through Building Carbon Nanosphere Coatings

Nondestructive Strategy to Effectively Enhance the Interfacial Adhesion of PBO/Epoxy Composites

Interface Properties of Composites from PBO Fibers Modified by Polyurethane Sizing Agent

Branched Fluorine/Adamantane Interfacial Compatibilizer for PBO Fibers/Cyanate Ester Wave-Transparent Laminated Composites

The influence of sizing treatment on the mechanical and morphological properties of carbon fiber reinforced polyphenylene sulfide composites

A novel thermoplastic water-soluble sizing agent for the interfacial enhancement of carbon fiber/polyether ether ketone composites

Enhanced mechanical and tribological properties of carbon fiber/PEEK composites by hydroxylated boron nitride nanosheets and polyetherimide sizing agents

Enhancing interfacial adhesion and mechanical performance of PBO fibers composites through mussel‐inspired molecular regulation of interphase structure

PBO fibers/fluorine-containing liquid crystal compound modified cyanate ester wave-transparent laminated composites with excellent mechanical and flame retardance properties

High-performance carbon fiber-reinforced epoxy resin composites based on novel, environmentally friendly, stability, and heat-moisture resistant nano emulsion encapsulated POSS sizing agent interface modification

Boosting interfacial adhesion in PBO fiber/epoxy composite by employing finely granular-structured polyaniline as an interfacial intensifier

Effect of polyetherimide sizing on surface properties of carbon fiber and interfacial strength of carbon fiber/polyetheretherketone composites

Water-based PEKC-COOH sizing agent for enhancing the interfacial adhesion of carbon fiber/polyether-ether-ketone composites

Synergistically enhanced interfacial and wave-transparent properties of PBO fiber composites: Constructing self-assembly interphase with different dimensional COF

Phthalocyanine-terminated poly(aryl ether) sizing: An efficient strategy in interfacial interactions optimization of CF/PPESK composites with excellent thermal-resistant

Surface modification of PBO fibers by direct fluorination and corresponding chemical reaction mechanism

Construction of solvent-resistant interphase of CF/PEEK composites via introducing water-based crosslinkable polyaryl ether sizing agent

Random copolymer membrane coated PBO fibers with significantly improved interfacial adhesion for PBO fibers/cyanate ester composites

Facile and environment-friendly mussel-inspired surface modification of PBO fibers via dopamine/3-aminopropyltrimethoxysilane co-deposition for advanced composite

Water-based PES-NaPSS sizing agent without surfactant for interface enhancement of CF/PEEK composites