Abstract:Cracking in fibrous composites is inevitable, and the fracture pattern is influenced by its fiber distribution. Bamboo fibrous composites have a distinct fiber distribution, which makes them an excellent material for studng the relationship between fiber distribution and fracture mode. Glued laminated bamboo is a bi-directional bamboo fibrous composite, which is called glubam for short. Its vertical thickness is about 28 mm, and the ratio of the number of longitudinal fiber layers to the number of transverse fiber layers is 4:1. This study conducted three-point bending fracture tests on single-edge notched specimens of glubam to investigate its mode-I fracture characteristics in the transverse vertical direction. The deformation curves show that the specimens still have the load-carrying capacity after reaching the maximum load, and the load shows a trend of step-like decrease, exhibiting a quasi-ductile fracture behavior. Overall, the fracture process can be divided into four stages, including linear, softening, quasi-ductile, and failure stages. In this study, based on certain assumptions, the prefabricated notch length a0 was adjusted according to the position of the transverse fibers. Subsequently, the non-linear elastic fracture mechanics method was employed to calculate the fracture parameters of glubam during the softening and quasi-ductile stages, including the fracture toughness KIC* and fiber tensile strength ft. The deviation of the fracture parameters between the two stages is within 10%, indicating that the correction of the a0 is correct. This indirectly proves that the staggered structure formed by longitudinal and transverse fibers is responsible for the quasi-toughness fracture of glubam. Finally, this study summarized and analyzed the quasi-ductile fracture behavior and found that materials or structures exhibiting quasi-ductile fracture behavior often possess a staggered structure. This staggered structure makes the crack in the form of semi-stable propagation, while the load decreases in a step-like manner.

Mode I Fracture Behavior of Unidirectional Bamboo Laminate and Its Applications to the Estimation of Bamboo-Steel-bamboo Connections’ Bearing Capacities

Mechanical Behavior of Glued Laminated Bamboo Moment-Resisting Connections

Experimental study on mechanical behavior of glue laminated bamboo Ⅰ-joists

The Off-Axis Embedment Performance of Bamboo Panels Used for Glubam Structures

Experimental investigation on shear behavior of full-scale glued laminated bamboo beams under three-point loading test and using digital image correlation technique

Monotonic and cyclic tests of round bamboo shear walls

Experimental Investigation and Evaluation of Metal-Plate-connected Laminated Bamboo Lumber Joints

Bending Performance of Nail-Laminated Bamboo-Timber Panels Made with Glubam and Fast-Grown Plantation Chinese Fir

Effect of crack size, thickness and span on the transverse mode I fracture characteristics of laminated flattened-bamboo lumber

Mode I Fracture Toughness of Tangential Moso Bamboo

Tangential Fracture Toughness of Bamboo

Real-time flexural fracture behaviors and toughening mechanisms of bamboo slivers with different fiber content and moisture content

In Situ Observation of Fracture Behavior of Bamboo Culm

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

In Situ Detection of the Fracture Behaviour of Moso Bamboo (phyllostachys Pubescens) by Scanning Electron Microscopy

Bamboo as a substitute for plastic: Underlying mechanisms of flexible deformation and flexural toughness of bamboo at multiple scales

The study on in situ asymmetric bending behavior of structural bamboo materials under combined tension-bending loads

Study on the Quasi-Ductile Fracture Behavior of Glubam: The Role of Fiber Distribution

Structural performance of laminated-bamboo lumber nailed connection

Research on Moso Bamboo Radical Fracture Toughness

Compressive Failure Mechanism of Structural Bamboo Scrimber