Abstract:Cross-laminated bamboo (CLB) is a bamboo-based construction product with bamboo's advantages, which are green, environmentally protective, and sustainable. However, bamboo is easy to crack. Structural elements in bamboo constructions are assembled onsite, making splitting cracks easily form at joints and bolt connections. Therefore, it is essential to assess cracked structure safety with fracture mechanics. However, rare studies are addressed on fracture properties of bidirectional laminated bamboo, especially the translaminar fracture resistance, which represents the ability to arrest a catastrophic crack in structures. This paper studies the translaminar fracture properties of CLB composite using three-point bending beam tests. Load-displacement and load-CMOD curve characteristics, fracture process, and the failure modes of bidirectional laminated bamboo are analyzed. The R-curve expressed by the energy release rate is calculated by three methods. Results demonstrate that the Rcurves obtained by the three different methods show similar results. The methods to determine R-curves employed in this study are simple and can describe the translaminar fracture toughness of laminated bamboo. The methods are validated by comparing the traction-separation relations calculated from the R-curves to those measured by double-edge notched tests (DENT). A comparison of the bidirectional laminated bamboo's energy release rate to the matrix-dominated energy release rate of unidirectional laminated bamboo reveals that bidirectional fiber arrangement has a remarkable improvement on the toughening of laminated bamboo at and after crack initiation. Moreover, the lay-up effects of CLB are analyzed by relating the energy release rate results to the failure pattern of fractured specimens. It is found that fiber pullout/bridging caused by 90 degrees direction crack propagation around fiber bundles is the dominant toughening mechanism of CLB. The lay-up sequence of 0 degrees and 90 degrees plies also has an effect on 90 degrees direction crack propagation; therefore, it will influence the toughness of CLB.

In Situ Observation of Fracture Behavior of Bamboo Culm

In Situ Detection of the Fracture Behaviour of Moso Bamboo (phyllostachys Pubescens) by Scanning Electron Microscopy

Three-point bending fracture behaviors of bamboo

Real-time flexural fracture behaviors and toughening mechanisms of bamboo slivers with different fiber content and moisture content

Tangential Fracture Toughness of Bamboo

Experimental Investigation on Translaminar Fracture Behavior of Cross-Laminated Bamboo

The study on in situ asymmetric bending behavior of structural bamboo materials under combined tension-bending loads

Mode I Fracture Behavior of Unidirectional Bamboo Laminate and Its Applications to the Estimation of Bamboo-Steel-bamboo Connections’ Bearing Capacities

Mode I Fracture Toughness of Tangential Moso Bamboo

Asymmetric Flexural Process and Fracture Behaviors of Natural Bamboo Node with Gradient Discontinuous Fibers

Experimental Study of the Fracture Behavior of Bamboo Under Tension Based on Digital Speckle Correlation Method

Bamboo as a substitute for plastic: Underlying mechanisms of flexible deformation and flexural toughness of bamboo at multiple scales

Mode II Fracture Behavior of Parallel Strand Bamboo Measured by 3-Point End-Notched Flexure Tests

Experimental Investigation Of The Mixed-Mode Crack Expanding In Bamboo

Micro/nanoscale mechanical characterization and in situ observation of cracking of laminated Si3N4/BN composites

Research on Moso Bamboo Radical Fracture Toughness

Study on the Quasi-Ductile Fracture Behavior of Glubam: The Role of Fiber Distribution

Compressive Failure Mechanism of Structural Bamboo Scrimber

Flexural deformation and fracture behaviors of bamboo with gradient hierarchical fibrous structure and water content

Tensile Behaviour and Fracture Mechanism of Moso Bamboo (phyllostachys Pubescens)

Bamboo's tissue structure facilitates large bending deflections