Abstract:For an accurate estimation of the fatigue performance of welded joints, not only the initial residual stress field but also its variation under load is decisive. The portion of residual stress which stays stable can shift the load stress range much the same way as the mean stresses do in fatigue loading. The relaxation of residual stresses during fatigue loading however reduces this hazard to the structural health. That is, before considering the influence of residual stresses in fatigue, the effect of fatigue on residual stresses should be understood. In this work, the influence of the quasi-static and cyclic loading on the relaxation of welding residual stresses in small specimens and large components out of different steels namely S235JRG2, S355J2G3, P460NL, S690QL, S960QL, and S1100QL has been investigated experimentally. X-ray diffraction analysis as a reliable method has been used for the determination of residual stress profiles in surface layers. For residual stress analysis in deeper layers, synchrotron and neutron diffraction techniques were applied as complementary methods. A clear recognition of the difference between initial welding residual stresses in small- and large-scale specimens was observed. Tensile residual stresses as high as the yield strength could appear in large-scale welded specimens. That was not the case for small-scale welds due to the low grade of restraint. Nevertheless, in both types of samples, the highest residual stresses were obtained in the weld centerline. At the weld toe which is critical regarding fatigue crack initiation, the magnitude of the residual stresses is lower. Beside of that, it was observed that in the case of relaxation, the first load cycles especially in components out of low-strength steels are decisive. The influence of loading conditions and local mechanical properties on the relaxation of welding residual stresses was investigated based on principles of solid mechanics. The von Mises failure criterion was able to describe the relaxation behavior.

An Investigation on Residual Stress and Fatigue Life Assessment of T-shape Welded Joints

Study on Fatigue Performance of T Shape Joint

Fatigue Testing in Welded Joint of 980- grade Steels

Finite element simulation of multi-layer repair welding and experimental investigation of the residual stress fields in steel welded components

Fatigue life improvement using low transformation temperature weld material with measurement of residual stress

Welding residual stress behavior under mechanical loading

Exploring Through-Thickness Residual Stress Distribution in Double V-Groove Multipass Welds of High-Strength Low-Alloy Steel and the Impact of Mechanical Restraints

Distribution of longitudinal inherent strains in multiple-passes welding

Influence of welding residual stress and welding method on fracture properties of welded joints

Influence of Repair Welding on the Fatigue Behavior of S355J2 T-Joints

Fatigue Strength and Fatigue Fracture Mechanism for Spot Welds in U-Shape Specimens

A Fatigue Life Prediction Approach for Resistance Spot Welded Joints with Consideration of the Stress Ratio Effect

A practical analysis of residual stresses induced by high-frequency mechanical impact post-weld treatment

Fatigue Strength Assessment of Friction Welds under Consideration of Residual Stress

FE analysis of residual stress and welding deformation of a low-alloy UHS quenched steel fillet joint

Evaluation of Thickness Effect on Fatigue Life Variation of Longitudinal Welded Gusset Joint

Evaluation of multiple residual stress components in a thick welded joint using extended contour method

Study on Fatigue Behavior and Crack Propagation Life of Longitudinal Fillet Welded Lap Joint

The effect of residual stress on fatigue life of welded Cruciform joints of 16MnR for train bogie

Fatigue experiment and assessment of butt-welded joints in steel structures considering misalignment and weld geometry effects

Numerical Investigation on Optimizing Fatigue Life in a Lap Joint Structure