Rapidly Quenched Heavy Rare Earth-Based Ternary Lu-Fe-B Alloys: Phase Evolution and Hard Magnetic Properties

Bang Zhou,Songmao Li,Wenbing Fan,Xuefeng Liao,Jiayi He,Hongya Yu,Zhongwu Liu

DOI: https://doi.org/10.1016/j.mtcomm.2022.104124

IF: 3.8

2022-01-01

Materials Today Communications

Abstract:Aiming to clarify the fundamental properties of Lu-Fe-B alloys and facilitate the application of the Lu in rare earth (RE)-iron-boron permanent magnets, the phase constitutions, phase precipitation behavior, and hard magnetic properties of Lu12+xFe82-xB6 alloys (x = 0-4) prepared by melt spinning were systematically studied. The intrinsic coercivity H-cj= 313 kA/m, remanence J(r) = 0.72 T, and maximum energy product (BH) max = 68.5 kJ/m(3) were obtained in optimally quenched Lu(12)Fe(82)13(6) alloy. Different from many other RE-Fe-B alloys, increasing Lu content leads to the formation of the soft magnetic amorphous phase and Lu6Fe23 phase, which eventually increases the exchange coupling effect and decreases H-cj and (BH)(max) of the Lu-rich alloys (x = 1-4). For the amorphous Lu12+xFe82-xB6 alloys, after annealing treatment, Lu2Fe14B and Fe2B phases precipitate in the alloys with x = 0 and 1, but the crystalline phases change into Lu6Fe23, Lu2Fe14B, and Fe2B phases in the alloys with x = 2-4. For the Lu-rich alloys, all crystalline phases tend to precipitate simultaneously from the amorphous matrix, which is beneficial to obtaining optimized microstructure under various processes. The alloy with x = 2 annealed at 750 degrees C for 10 min exhibits a good combination of magnetic properties with J(r) = 0.69 T, H-cj= 234 kA/m, and (BH)(max) = 51.9 kJ/m(3). The present results can serve as a useful reference for promoting the utilization of Lu in RE permanent magnets.